废铝熔体中去除Cr元素的试验研究  

Experiments of removing Cr from waste Al slag melts

作　　者：孙德勤[1] 戴国洪[1] 徐越[2] 

机构地区：[1]常熟理工学院化学与材料工程学院,江苏常熟215500 [2]中国矿业大学材料工程学院,江苏徐州221116

出　　处：《轻合金加工技术》2016年第1期24-28,共5页Light Alloy Fabrication Technology

基　　金：苏州市自然科学基金资助项目(项目编号:SYG201101)

摘　　要：废铝合金中Cr元素含量过高会降低其塑性加工性能和材料的使用性能。分析了熔剂法去除废铝熔体中cr元素的工艺原理，设计除Cr工艺试验方案。结果表明，熔剂的组成为活性炭＋MnCl2（质量比1：2），加入量为1％～1．5％（质量分数）并静置时间为30min左右，在铝熔体浇注时采用过滤处理的工艺条件下，可以达到较为满意的除Cr效果。Excessive content of Cr in A1 alloys would reduce plastic deformation ability and usability. Process principles have been analyzed for Cr-removing from the waste A1 slag melts by fluxing technology. The Cr removing scheme has been designed and the process experiments have been carried out. The results show that the desired effects of Cr removing can be achieved when I% - 1.5% （mass fraction） fluxing-agents are added into the melting and held for 30 rain,with active carbon and MnC12 1 ： 2 （ mass ratio） composed, and when A1 melt filtration is used in casting.

关 键 词：废铝再生 除Cr反应 熔剂法 工艺控制 

分 类 号：TG292[金属学及工艺—铸造]