Al-Co-Y三元系合金873K等温截面的研究  

Study on Isothermal Section of Al-Co-Y System Aolly at 873 K

作　　者：李显[1] 刘立斌[1,2] 毋敌 王星[1] 章立钢[1] 

机构地区：[1]中南大学材料科学与工程学院,湖南长沙410083 [2]有色金属材料科学与工程教育部重点实验室,湖南长沙410083

出　　处：《铸造技术》2016年第1期14-17,共4页Foundry Technology

摘　　要：采用合金法，通过电子探针微区成分分析和X射线衍射仪物相等实验方法分析确定了Al—Co—Y三元系在873K时部分相关系。实验获得了5个三元化合物，分别为Al7Co2Y、Al9Co3Y2、Al2CoY、AlCoY及AlCo2Y2。其中，AlCo2Y2为新相。Al2Y和Co2Y在三元系中固溶度范围分别为0～8．2at．％Co和0-7.8at．％Al，而能谱分析显示Al在Co3Y、Co5Y和Co17Y2在体系中有很大的固溶度范围，实验测定值分别为31．8at．％Al、32．4at％Al和24．1at．％Al。With the equilibrium alloy method, the partial phase relations of Al-Co-Y system alloy were measured by the electron probe microanalysis and X-Ray Diffraction. Five ternary compounds i.e., Al7Co2Y、Al9Co3Y2、Al2CoY、AlCoY and AlCo2Y2 were determined in the system. Among them, A1Co2Y2 was found to be a new compound. The solid solubility range of Co in Al2Y is about 0-8.2 at.% Co and Al in Co2Y is about 0-7.8 at.% Al in this system, but Co3Y, Cosy and Co17Y2 have a large homogeneity region, the experimental data are 31.8 at.% Al, 32.4 at.% Al and 24.1 at% Al, respectively.

关 键 词：合金法 相平衡 等温截面 

分 类 号：TG146.21[一般工业技术—材料科学与工程]