钛酸锶钡(Ba_(0.6)Sr_(0.4)TiO_3)纳米粉体的微波水热法合成  

Synthesis of Barium and Strontium Titanate (Ba_(0.6)Sr_(0.4)TiO_3) Nanopowders by Microwave Hydrothermal Method

作　　者：王绍钢[1,2] 赵青[1] 常爱民[1] 杨忠波[1,2] 

机构地区：[1]中国科学院新疆理化技术研究所 [2]中国科学院研究生院,北京100089

出　　处：《材料导报》2007年第S2期95-98,108,共5页Materials Reports

基　　金：国家自然科学基金资助项目(No.50372083);中国科学院新疆理化技术研究所创新方向性资助项目(No.03200454002003)

摘　　要：采用微波水热法成功合成了钛酸锶钡(Ba0.6Sr0.4TiO3)纳米粉体。研究了反应温度、反应时间和反应物浓度对微波合成的影响。结果表明:微波合成的最佳制备条件为反应温度195℃,反应时间20～30min,Ba2+: Sr2+:Ti4+=3:2:1,Ba(NO3)2浓度为0.12mol/L,KOH浓度为0.6mol/L。在以上工艺参数条件下,能获得分布均匀,结晶完好,平均粒径为60nm的Ba0.6Sr0.4TiO3纳米粉体。Ba0.6Sr0.4TiO3(BST) nanopowders are successfully synthesized by microwave-hydrothermal (MH) method. The effects of reaction temperature; reaction time, and reactant composition on MH synthesis of BST are investigated. Well-dispersed and narrowly distributed BST nanopowders of about 60nm are obtained when samples, having a molar ratio of Ba(NO3)2 : Sr(NO3)2 : Ti(C4H9O)4 of 3 : 2 : 1, and an initial concentration of Ba(NO3)2 and KOH at 0.12mol/L and 0.6mol/L,respectively,are heated to 195℃,for 20 to 30min.

关 键 词：微波水热 钛酸锶钡 纳米粉末 

分 类 号：TB383.1[一般工业技术—材料科学与工程]