工艺条件对高温黑釉影响的研究  

Effects of Processing Condition on High-temperature Black Glaze

作　　者：董伟霞[1] 包启富[1] 常启兵[1] 汪永清[1] 刘云[1] 

机构地区：[1]景德镇陶瓷学院,江西景德镇333001

出　　处：《陶瓷》2016年第1期38-39,共2页Ceramics

摘　　要：笔者以工业尾矿（如铁、钴等尾矿）为着色原料代替传统的金属氧化物制备了颜色纯正的高温黑釉。实验结果证明：工艺条件对高温黑釉有着明显的影响，当釉层厚度为1．0～1．5mm，烧成温度为1270-1300℃，保温时间为12～15min时，在氧化气氛下可以烧制出颜色纯正，釉面光滑的黑釉。In the paper, high-temperature matt black glaze were prepared using tailings i. g. chromium tailings, cobalt tailings, as coloring agents replacement of the traditional metal. The results showed that processing condition is important for the high-temperature black glaze. When the glaze thickness is 1. 0-1.5 mm, firing temperature of 1 270-1 300℃ and soaking time of 12-15 rain, the black glaze with the smooth surface is prepared.

关 键 词：金属尾矿 高温黑釉 工艺条件 

分 类 号：TQ174.4[化学工程—陶瓷工业]