一种浸渍式钨酸盐阴极的制备与发射性能  被引量:5

Fabrication and Emission Characteristics of Impregnated Tungstate Cathode

在线阅读下载全文

作  者:胡明玮[1,2] 王小霞[1] 罗积润[1] 漆世锴[1,2] 李云[1] 

机构地区:[1]中国科学院电子学研究所高功率微波源与技术重点实验室,北京100190 [2]中国科学院大学,北京100049

出  处:《真空科学与技术学报》2016年第1期28-32,共5页Chinese Journal of Vacuum Science and Technology

摘  要:本文开展了活性物质为钨酸钡锶的浸渍式钨酸盐钡钨阴极的研究,主要包括钨酸钡锶盐的合成,浸渍式钨酸钡锶阴极的制备及其发射性能的测试。实验结果表明:在1400℃空气气氛中合成了主要相为Ba_3WO_6及Ba_2SrWO_6的钨酸钡锶盐。在1800℃浸渍该钨酸盐与氢化锆的混合物成功制备了浸渍式钨酸盐阴极,阴极发射性能测试结果表明在1050℃_(br)和1000℃_(br)时直流发射电流密度分别为7.54和4.30 A/cm^2。A novel type of the impregnated tungsten cathode activated by Ba-Sr tungstate was fabricated.The influence of the fabrication conditions,including but not limited tothe synthesis temperature of Ba-Sr tungstate,impregnation temperature of a mixture of tungstate and zirconium hydride,and porosity of tungsten base,on the emission characteristics of the cathode was investigated with X-ray diffraction,scanning electron microscopy,and energy dispersive spectroscopy.The results show that the fairly uniform stable DC emission current density of the cathode reaches 7.54 A/cm^2 at1050℃_(br) and 4.30 A/cm^2 at 1000℃_(br),respectively,impregnated at 1800℃ with Ba-Sr tungstate sintered at 1400℃ in air and existing mainly in the phases of Ba_3WO_6 and Ba_2SrWO_6.

关 键 词:钨酸盐阴极 钨酸钡锶 X射线衍射分析 发射电流密度 

分 类 号:O462[理学—电子物理学]

 

参考文献:

正在载入数据...

 

二级参考文献:

正在载入数据...

 

耦合文献:

正在载入数据...

 

引证文献:

正在载入数据...

 

二级引证文献:

正在载入数据...

 

同被引文献:

正在载入数据...

 

相关期刊文献:

正在载入数据...

相关的主题
相关的作者对象
相关的机构对象