Effect of oxygen-containing additives on weld penetration in self-shielded flux cored arc welding  

作　　者：张占伟 李午申 

机构地区：[1]School of Materials Science and Engineering, Tianjin University, Tianjin, 300072. [2]School of Materials Science and Engineering, Shenyang Aerospace University, Shenyang, 110136.

出　　处：《China Welding》2015年第4期64-68,共5页中国焊接（英文版）

摘　　要：The effect of Fe203 and Liz CO3 additives in flux core on the weld metal oxygen content and weld penetration in self-shielded flux cored arc welding were studied schematically. The result shows that the oxygen content in the weld metal and weld penetration both increased with the Fe203 addition increased in the range of 5 wt. % to 20 wt. %. The oxygen content in the weld metal was increased with the Li2CO3 addition increased in the range of 1 wt. % to 8 wt. %. However, the weld penetration decreased when Li2CO3 addition exceeding 4 wt. %. High-speed photographic images show that when Fe2O3 addition influx core exceeding 15 wt. %, droplet became excessively large, so that spatters were frequently generated in large numbers. In this study, Fe203 and Li2 CO3 in the amount of 11 wt. % and 4 wt. %, respectively, jointly added in the flux core can achieve a deeper weld penetration with sound usability characteristics.The effect of Fe203 and Liz CO3 additives in flux core on the weld metal oxygen content and weld penetration in self-shielded flux cored arc welding were studied schematically. The result shows that the oxygen content in the weld metal and weld penetration both increased with the Fe203 addition increased in the range of 5 wt. % to 20 wt. %. The oxygen content in the weld metal was increased with the Li2CO3 addition increased in the range of 1 wt. % to 8 wt. %. However, the weld penetration decreased when Li2CO3 addition exceeding 4 wt. %. High-speed photographic images show that when Fe2O3 addition influx core exceeding 15 wt. %, droplet became excessively large, so that spatters were frequently generated in large numbers. In this study, Fe203 and Li2 CO3 in the amount of 11 wt. % and 4 wt. %, respectively, jointly added in the flux core can achieve a deeper weld penetration with sound usability characteristics.

关 键 词：self-shielded flux cored wire weld penetration OXYGEN surface tension 

分 类 号：TG422.3[金属学及工艺—焊接] TG457.14