硅氧烷官能化聚芳醚腈自组装膜的制备及其性能  

Preparation and Properties of Triethoxysilane Functionalized Poly( phthalazinone ether nitrile) Self-Assembled Thin Films

作　　者：靳奇峰[1] 姜冬月 佟丽娜[1] 蹇锡高[2] 

机构地区：[1]辽宁师范大学化学化工学院,辽宁大连116021 [2]大连理工大学化工学院高分子材料系,辽宁大连116012

出　　处：《应用化学》2016年第2期169-174,共6页Chinese Journal of Applied Chemistry

基　　金：辽宁省博士启动基金资助项目(20111066)~~

摘　　要：杂萘联苯聚芳醚腈通过水解、酰化及氨丙基三乙氧基硅烷改性后,合成了侧链含有硅氧烷官能团功能性聚芳醚树脂(PNAS)。采用红外、1H NMR、固体29Si NMR谱等技术手段对产物结构进行表征,用DSC、TGA和原子力显微镜测试了PNAS树脂的性能和自组装薄膜的表面形貌。结果表明,PNAS具有优异的耐热性,其玻璃化转变温度为329℃,热失重温度(T5%)达到492℃。与短链分子自组装膜比较,PNAS自组装薄膜具有良好的减摩抗磨性能,当载荷为400 m N时,自组装薄膜的稳定摩擦系数达到0.07且在5 h内基本不变。A novel triethoxysilyl-functionalized poly（ phthalazinone ether nitrile）（ PNAS） was synthesized by hydrolysis,acylation and 3-aminopropyltriethoxysilance-functionalization,and characterized by FTIR,^29 Si NMR,DSC and TGA. The self-assembled polymer film was designed to serve as wear resistant coating for silicon surface. It has an excellent heat-resistance with a glass transition temperature and the temperature at which 5% mass loss at 329 ℃ and 492 ℃,respectively. The surface morphology of self-assembled film was studied by atomic force microscopy,while the friction performance was investigated using reciprocating friction tester. Comparing with the short chain self-assembled film,the friction coefficient of the prepared film is very low（ about 0. 07 at the loading of 400 n N）,and the anti-wear behavior is good,with a lack of failure after sliding over 5 hours.

关 键 词：聚芳醚腈 自组装膜 摩擦学性能 润滑 

分 类 号：O631.5[理学—高分子化学]