纳米结晶纤维素改善脲醛树脂胶黏剂游离甲醛的研究  

Reduction of Free Formaldehyde Emission from Urea-formaldehyde Resin Adhesive by Use of Modified Nanocrystalline Cellulose

作　　者：张浩[1] 蒲俊文[2] 洪亮[1] 朱明[1] 

机构地区：[1]河南工程学院材料与化学工程学院,河南郑州450000 [2]北京林业大学材料科学与技术学院,北京100083

出　　处：《林产化学与工业》2016年第1期99-104,共6页Chemistry and Industry of Forest Products

基　　金：河南工程学院轻化工程技术研究中心建设项目(GCZX2013003);河南省高等学校重点科研项目(15A430019)

摘　　要：为了降低脲醛树脂胶黏剂的游离甲醛释放量,以俄罗斯落叶松浆粕为原料,利用酸水解,硅烷偶联剂改性等制备获得表面改性纳米结晶纤维素（M-NCC）,并将M-NCC作为吸附材料用于脲醛树脂基材制备胶合板,研究M-NCC对脲醛树脂胶黏剂游离甲醛的吸附效果和机理。结果表明：透射电镜（TEM）检测可知,制备的NCC颗粒长度约为100~200 nm、直径约为20~30 nm,结晶度为57.3%,相比原始纤维素提高了41.1%;硅烷偶联剂3-（2-氨乙基）-氨丙基甲基二甲氧基硅烷（MCPS）使NCC的浸润性显著增强,当MCPS用量为8%时M-NCC接枝率达到27.2%,M-NCC对脲醛树脂的接触角为65.7°,下降32.7%;由扫描电镜（SEM）照片可观测到,表面改性显著改善了低浓度NCC颗粒在脲醛树脂基材中的分散状态,当M-NCC质量分数2%时,纳米颗粒的分散性能明显下降;M-NCC可有效吸附脲醛树脂基材中的游离甲醛,当M-NCC质量分数1.5%时可致游离甲醛比对照组（0.51 mg/L）下降50.9%。In this study,a modified nanocrystalline cellulose（ M-NCC） was used to reduce the free formaldehyde emission from urea-formaldehyde resin adhesive. M-NCC was prepared by a procedure that Russian larch pulp was hydrolyzed by acid,followed by the modification of 3-（ 2-aminoethyl）-aminopropylmethyldimethoxysilane（ MCPS）. The effects of M-NCC on the emission of free formaldehyde from urea-formaldehyde resin adhesive were analyzed. The results indicated that from the TEM images,the length of the nanocrystalline cellulase（ NCC） particles prepared by acid hydrolysis was 100- 200 nm,and the diameter was 20-30 nm. Compared with the original cellulose,the crystallinity degree of NCC was improved by 41. 1 %. The wetting property of M-NCC was enhanced by the graft of MCPS. The contact angle between M-NCC and urea-formaldehyde resin adhesive was decreased by 32. 7 % when the grafting ratio was 27. 2 %. The SEM images showed that the disperse state of M-NCC particles under low concentrations was improved significantly and the dispersity of nano-partides decreased obviously as the M-NCC was 2 %.Free formaldehyde was absorbed by the M-NCC and 1. 5 % M-NCC led to a 50. 9 % decline of the emission of free formaldehyde.

关 键 词：纳米结晶纤维素 改性 脲醛树脂 游离甲醛 

分 类 号：TQ35[化学工程] TS727[轻工技术与工程—制浆造纸工程]