月桂酸钠修饰纳米银颗粒的化学还原法制备与表征  

Synthesis and Characterization of Sodium Laurate Capped Silver Nanoparticles by Chemical Reduction Method

作　　者：程菲[1,2] 董春法[2] 李宏[1] 王向杰[2] 

机构地区：[1]湖北师范学院物理与电子科学学院,湖北黄石435002 [2]湖北理工学院机电工程学院,湖北黄石435003

出　　处：《湖北理工学院学报》2016年第1期18-22,共5页Journal of Hubei Polytechnic University

基　　金：国家自然科学基金青年科学基金项目(项目编号:51405146);湖北理工学院校级科研项目(项目编号:15xjz04R)

摘　　要：为制备粒径较小、分布均匀、稳定的纳米银溶胶,以月桂酸钠为保护剂,水合肼为还原剂,硝酸银溶液为前驱体,采用化学还原法进行试验。试验结果表明,保护剂与还原剂的用量对纳米银的粒径有着较大的影响。当保护剂用量为0.5 g、水合肼用量为1.0 g时,所得到的纳米银粒子平均粒径为5~7 nm。In order to prepare stable silver nanoparticles with narrow distribution, a simple route in water was used, with sodium laurate as the protecting agents, hydrazine hydrate as reducing agents, silver nitrate solution as precursor. The results showed that the dosage of the protecting agents and reducing agents play an impor- tant role in the formation of small size silver nanoparticles with narrowly distribution. Well - dispersed silver anopartilces with average diameter of 5 to 7 nm were obtained when the dosage of protecting agents was 0.5 g and the dosage of reducing agents was 1.0 g.

关 键 词：月桂酸钠 纳米银 化学还原法 纳米粒子 

分 类 号：TB383[一般工业技术—材料科学与工程]