Comprehensive Optimization of Electrical and Optical Properties for ATO Films Prepared by Pulsed Laser Deposition  

作　　者：SHEN Qiang YANG Ping LI Na LI Meijuan 陈斐 ZHANG Lianmeng 

机构地区：[1]State Key Laboratory of Advanced Technology for Materials Synthesis and Processing,Wuhan University of Technology [2]Department of Chemical Engineering and Materials Science,University of California

出　　处：《Journal of Wuhan University of Technology(Materials Science)》2016年第1期20-26,共7页武汉理工大学学报（材料科学英文版）

基　　金：Funded by the International Science&Technology Cooperation Program of China(No.2011DFA52650);the"111"Project(No.B13035);the National Natural Science Foundation of China(No.51521001);the Fundamental Research Funds for the Central Universities

摘　　要：Antimony doped tin oxide（ATO） thin films have been prepared by pulsed laser deposition（PLD） method.The intrinsic effect of Sb dopant,including the Sb content,transition degree between Sb（3＋） and Sb（5＋） and crystallinity on the electrical and optical properties of the ATO thin films is mainly investigated.It is suggested that the transition degree of Sb（3＋） towards Sb（5＋）（Sb（5＋）/Sb（3＋） ratio） is determined by Sb content.When the Sb content is increased to 12 at%,the Sb（5＋）/Sb（3＋） ratio reaches the highest value of 2.05,corresponding to the resistivity of 2.70×10（-3） Ω·cm.Meanwhile,the Burstein-Moss effect caused by the increase of carrier concentration is observed and the band gap of the ATO thin films is broadened to 4.0 eV when the Sb content is increased to 12 at%,corresponding to the highest average optical transmittance of 92%.Comprehensively considering the combination of electrical and optical properties,the ATO thin films deposited with Sb content of 12 at%exhibit the best properties with the highest ＂figure of merit＂ of 3.85×10（-3） Ω（-1）.Finally,an antimony selenide（Sb_2Se_3） heterojunction solar cell prototype with the ATO thin film as the anode has been prepared,and a power conversion efficiency of 0.83%has been achieved.Antimony doped tin oxide（ATO） thin films have been prepared by pulsed laser deposition（PLD） method.The intrinsic effect of Sb dopant,including the Sb content,transition degree between Sb（3＋） and Sb（5＋） and crystallinity on the electrical and optical properties of the ATO thin films is mainly investigated.It is suggested that the transition degree of Sb（3＋） towards Sb（5＋）（Sb（5＋）/Sb（3＋） ratio） is determined by Sb content.When the Sb content is increased to 12 at%,the Sb（5＋）/Sb（3＋） ratio reaches the highest value of 2.05,corresponding to the resistivity of 2.70×10（-3） Ω·cm.Meanwhile,the Burstein-Moss effect caused by the increase of carrier concentration is observed and the band gap of the ATO thin films is broadened to 4.0 eV when the Sb content is increased to 12 at%,corresponding to the highest average optical transmittance of 92%.Comprehensively considering the combination of electrical and optical properties,the ATO thin films deposited with Sb content of 12 at%exhibit the best properties with the highest ＂figure of merit＂ of 3.85×10（-3） Ω（-1）.Finally,an antimony selenide（Sb_2Se_3） heterojunction solar cell prototype with the ATO thin film as the anode has been prepared,and a power conversion efficiency of 0.83%has been achieved.

关 键 词：antimony doped tin oxide pulsed laser deposition Sb content Sb_2Se_3 solar cell 

分 类 号：TB383.2[一般工业技术—材料科学与工程]