热处理对Fe基非晶涂层结构与性能的影响  

Effects of heat treatment on structure and properties of Fe-based amorphous coatings

作　　者：吴仡璇 罗强[1] 焦津[1] 沈军[1] 

机构地区：[1]同济大学材料科学与工程学院,上海201804

出　　处：《金属功能材料》2016年第1期12-16,共5页Metallic Functional Materials

基　　金：国家自然科学基金项目(51371127;51274151);上海市自然科学基金项目(13ZR1462400)

摘　　要：利用HVAF超音速火焰喷涂技术制备了Fe40Cr23Mo14C15B6Y2非晶合金涂层。并将涂层在550、600、665、716、760、811℃这6个温度下进行真空热处理。采用X射线衍射仪、差热分析仪、场发射扫描电子显微镜、显微维氏硬度仪、动态极化曲线对涂层进行结构和性能的研究。通过与原始状态下涂层进行对比发现,热处理后涂层会析出Fe、Cr、Mo的碳化物,使得涂层硬度明显升高,而同时也产生贫铬区和孔洞,使得涂层耐腐蚀性能降低。Fe-based amorphous alloy coatings（Fe40Cr23Mo14C15B6Y2）were deposited by high-velocity air fuel technology.The as-sprayed coatings were heat treated under 550、600、665、716、760、811 ℃,respectively.XRD,DSC,SEM,Vickers Indenter and Electrochemical measurements were used for the investigation on structure and properties of coatings.Compared to the as-sprayed coating,precipitate composed of（Fe,Cr,Mo）-carbide was observed in heat treated coatings,which lead to the increase of hardness and decrease of corrosion resistance.

关 键 词：Fe基非晶涂层 热处理 晶化相 耐腐蚀性能 硬度 

分 类 号：TG174.4[金属学及工艺—金属表面处理]