纳米碳酸钙湿式复合改性工艺探索  

Modification of Nano-CaCO_3 Particles via Wet Route

作　　者：李晓菎 向兰[1] 向英[1] 金涌[1] 

机构地区：[1]清华大学化工系,北京100084

出　　处：《材料科学与工程》2002年第3期367-370,共4页Materials Science and Engineering

基　　金：清华大学开放实验室测试基金资助项目

摘　　要：本文采用硬脂酸钠与水溶性磷铝酸脂对纳米碳酸钙进行湿式复合包覆 ,以改善纳米碳酸钙的表面性能。实验结果表明 :采用固含率为 18% (w v)的纳米碳酸钙悬浮液为原料 ,当硬脂酸钠与水溶性磷铝酸脂的加入量均为 3 0g 10 0gCaCO3 ,在 70℃处理 2 0min后 ,纳米碳酸钙的吸油值可降至 67ml 10 0g ,而活化度增至 98%。复合改性后碳酸钙在四氯化碳介质中的分散性得到明显改善 ,其团聚粒径由 3 5 0～ 5 5 0 μm降至 15 0The surface modification of nano CaCO 3 particles presented in the form of slurry (18%(w/v)of solid concentration)via wet route was studied in this paper.After being treated with stearate(3 0g/100g CaCO 3) and aluminum phosphor organic coupling agent(3.0g/100g CaCO 3)at 70℃ for 20min,the nano CaCO 3 particles showed a comparatively low value of oil adsorption(67 ml/100g) and a high activity(98%).The double modification method improved the dispersion of nano CaCO 3 particles in tetrachloromethane obviously,decreased the cluster size of nano CaCO 3 particles from 350—550μm to smaller than 150μm.

关 键 词：纳米碳酸钙 湿式改性 硬脂酸钠 磷铝酸酯 表面改性 复合改性工艺 

分 类 号：TQ132.32[化学工程—无机化工] TB383[一般工业技术—材料科学与工程]