9Ni钢焊接工艺适应性研究  

Study on welding qualifications of 9% nickel steel

作　　者：林文虎[1,2] 华学明[1,2] 蔡艳[1,2] 吴毅雄[1,2] 王欢 岑越 王定贺 

机构地区：[1]上海交通大学上海市激光制造与材料改性重点实验室,上海200240 [2]高新船舶与深海开发装备协同创新中心,上海200240 [3]沪东中华造船集团有限公司,上海200240 [4]伯乐焊接集团公司(中国),江苏苏州215000

出　　处：《焊接技术》2016年第3期43-47,共5页Welding Technology

基　　金：中华人民共和国工业与信息化部;财政部项目资助<新型液化天然气船液货围护系统预先研究>;上海市科委项目资助(14DZ1200400)

摘　　要：研究了9Ni钢药芯焊丝气体保护焊立焊(板厚25 mm)、埋弧焊横焊(板厚25 mm)、焊条电弧焊立焊和仰焊(板厚16 mm)不同焊接位置的焊接工艺。试验结果表明:焊缝表面成形良好,无焊接缺陷,其力学性能满足LNG船储罐低温材料的使用要求。The welding qualifications of 9% nickel steel was investigated at different welding conditions, such as flux cored arc welding at vertical position, submerged arc welding at horizontal position and shield metal arc welding at vertical and overhead position. The results showed that no-defects weld joints with good bead formation were obtained.The mechanical properties were satisfied with the specifications of LNG ship.

关 键 词：9NI钢 药芯焊丝气体保护焊 埋弧焊 焊条电弧焊 力学性能 LNG船 