预氧化对Fe-Cr-Al多孔材料抗硫化腐蚀性能的影响  

Effect of preoxidation on sulfidation resistance of Fe-Cr-Al porous materials

作　　者：谈萍[1] 陈金妹[1] 王建永[1] 葛渊[1] 李增峰[1] 康新婷[1] 杨保军[1] 贺卫卫[1] 

机构地区：[1]西北有色金属研究院金属多孔材料国家重点实验室,西安710016

出　　处：《功能材料》2016年第3期215-221,共7页Journal of Functional Materials

基　　金：陕西省科技统筹创新工程计划资助项目(2014KTZB01-02-04)

摘　　要：Fe-Cr-Al合金在高温下具有突出的耐高温、抗氧化、耐腐蚀性能,且力学性能优异,是洁净煤高温气体净化的理想材料。探讨了预氧化对Fe-Cr-Al多孔材料抗硫化腐蚀性能的影响。预氧化处理使材料表面生成了连续、致密的Al2O3阻挡层,有效地阻止了硫分子和金属离子的扩散,极大地提高了Fe-Cr-Al多孔材料的抗硫化腐蚀性能。Fe-Cr-Al alloy are regarded as the optimization materials for the cleaning coal gasification in high temperature purificatory,due to their good mechanical property,oxidation resistance and sulfide resistance at high temperature.This paper discussed the effect of pre-oxidation on sulfidation resistance of Fe-Cr-Al porous materials.It has formed continuous and compact Al2O3 countercheck film in Fe-Cr-Al alloy surface after preoxidation,which can be prevent the diffusion between S and metal ionic and improved the sulfide resistance greatly.

关 键 词：Fe-Cr-Al多孔材料 预氧化 抗硫化腐蚀 

分 类 号：TG172.3[金属学及工艺—金属表面处理]