纳米蒙脱土改性乳化沥青老化性能的研究  

Aging property of montmorillonite modified asphalt emulsion

作　　者：孙思萌[1,2] 李晓林[1,2] 郑广宇[1,2] 张立群[1,2] 

机构地区：[1]北京化工大学北京市新型高分子材料制备与加工重点实验室,北京100029 [2]北京化工大学有机无机纳米复合材料国家重点实验室,北京100029

出　　处：《化工新型材料》2016年第3期104-106,109,共4页New Chemical Materials

基　　金："863"计划课题"废轮胎胶粉改性利用关键技术"课题(2012AA063008)

摘　　要：采用旋转薄膜老化烘箱(RTFOT)对蒙脱土(MMT)改性乳化沥青、MMT改性沥青与有机化蒙脱土(OMMT)改性沥青的短期老化性能进行了测试,使用FT-IR与XRD对其改性机理进行了探究。结果表明:MMT改性乳化沥青的抗老化性能要远好于MMT改性沥青,与OMMT改性沥青的性能相当。当MMT掺量为2%时,MMT的层间距由1.28nm增加至4.74nm,增加了270%,改性乳化沥青的抗老化性能最好。Rotation thin film oven test（RTFOT）was conducted to simulate the short term aging of montmorillonite（MMT）modified asphalt emulsion,montmorillonite modified asphalt and organic montmorillonite（OMMT）modified asphalt,respectively.The modification mechanism was investigated by fourier transform infrared spectrometer（FT-IR）and Xray diffraction（XRD）.The results showed that MMT modified emulsified asphalt anti-aging performance was far better than that of MMT modified asphalt,and similar to the performance of the OMMT modified asphalt.When the content of MMT was 2%,the slice gap of MMT increased from 1.28 nm to 4.74 nm with a growth of 270%and the aging resistance of modified asphalt emulsion was best.

关 键 词：蒙脱土 乳化沥青 老化 

分 类 号：TE626.86[石油与天然气工程—油气加工工程]