漂白工艺对亚硫酸盐浆性能影响的研究  

Study on the Effect of Bleaching Process on Sulfite Pulp Properties

作　　者：熊钢[1] 刘文[2] 周立春[1] 郑艳民 金昌寿 李文刚 李鸿凯[1] 

机构地区：[1]中国制浆造纸研究院衢州分院,浙江衢州324000 [2]中国制浆造纸研究院,北京100102 [3]延边石岘白麓纸业股份有限公司,吉林图们133101

出　　处：《造纸科学与技术》2016年第1期16-19,81,共5页Paper Science & Technology

摘　　要：论文采用CED与DED漂白工艺对亚硫酸盐未漂辐射松溶解浆进行漂白,研究了E段用碱量、温度,DED漂白中D0段和D1段漂白参数对浆料性质的影响,获得了较优的漂白工艺。结果表明,CED漂白中,E段用碱量17%,碱处理温度95℃,漂后浆料的聚合度能够达到2019.6,白度91.0%ISO,α-纤维素96.19%。而采用DED漂白工艺,D0段二氧化氯用量1.5%,漂白时间3h,D1段用氯量0.45%,漂后浆料白度86.4%ISO,α-纤维素含量94.01%,聚合度2021.5。The original radiata pine sulfite dissolving pulp was bleached with CED and DED bleaching process in this paper. Effects of alkali dosage、temperature in E bleaching process and parameters in D0 and D1bleaching process on the properties of the bleached pulp were studied so as to obtain the optimum bleaching process The results showed that in CED bleaching process when alkali dosage was 17%,alkali treatment temperature was 95℃,bleached pulp polymerization degree,brightness,alpha cellulose can reach 2019. 6,91. 0% ISO,96. 19% respectively. While in DED bleaching process,when the amount of chlorine dioxide in D0 process was 1. 5%,bleaching time 3h,the amount of chlorine dioxide in D1 process was 0. 45%,bleached pulp polymerization degree,alpha cellulose,brightness can reach 2019. 6,96. 19%,91. 0% ISO respectively.

关 键 词：亚硫酸盐 二氧化氯 聚合度 Α-纤维素 

分 类 号：TS745[轻工技术与工程—制浆造纸工程]