聚合物/富勒烯太阳能电池形貌优化研究  

Research of Morphology Optimization of Novel Polymer/Fullerene Organic Solar Cells

作　　者：黄奎超 郑国敬 宋玉欣 张业容 刘策[1] 高博文[1,2] 

机构地区：[1]泰山学院机械与工程学院,泰安市271021 [2]曲阜师范大学物理工程学院,山东省曲阜市273165

出　　处：《曲阜师范大学学报（自然科学版）》2016年第2期73-77,共5页Journal of Qufu Normal University(Natural Science)

基　　金：泰安市大学生科技创新行动计划项目(2014D078);国家级大学生创新训练计划项目(201510453007)

摘　　要：选用苯并二噻吩和噻吩并吡咯(PBDTTPD)作为给体材料,和经典的受体材料富勒烯衍生物PC61BM/PC71BM搭配制作如下器件结构:氧化铟锡导电玻璃ITO(160nm)/阳极修饰层PEDOT:PSS(40nm)/活性层PBDTTPD:PCBM(90nm)/阴极修饰层LiF(0.5nm)/金属阴极Al(120nm).采用溶剂退火和添加剂后处理方法,利用有机溶剂慢蒸发过程以及溶剂和添加剂不同的沸点,使得给体和受体材料完成自组装,形成有序的给受体互联贯穿网状结构.结果表明,溶剂退火可以极大地优化PBDTTPD:PCBM活性层的形貌,最高能量转换效率(Power Conversion Effciency,PCE)达到4.95%.该实验成果可以为进一步提高聚合物/富勒烯有机太阳能电池的效率,提供有力的理论依据和实验指导.Highly efficient PBDTTPD-based photovoltaic devices with the configuration of Indium tin oxide（ITO）/poly（3,4-ethylenedioxythiophene）-poly（styrenesulfonate）（PEDOT∶PSS）/PBDTTPD∶methanofulle rene（6,6）-phenyl-C61/-butyric acid methyl ester（PC61BM）/LiF（0.5nm）/Al（100nm）,are realized with ortho-dichlorobenzene（oDCB）solvent annealing treatment.It is revealed that the best photovoltaic device is obtained when the blend ratio of PBDTTPD∶PC61BM is 1∶2and it is processed with oDCB solvent annealing for 12 hours.The short circuit current density（Jsc）and power conversion efficiency（PCE）value are measured to be 10.91mA/cm2 and 4.95%respectively,which are both higher than the counterparts treated with chlorobenzene（CB）solvent annealing or a processing additive（1%-3% v/v,chloronaphthalene）.Atomic force microscopy measurements of the active layer after the solvent annealing treatment are carried out.The phase separation length scale of the PBDTTPD∶PC61BM（1∶2）layers is comparable to the exciton diffusion length when the active layer is treated by oDCB solvent annealing,which facilitates effective exciton dissociation and carrier diffusion in the active layer.Therefore,highly efficient PBDTTPD-based photovoltaic devices can be achieved with oDCB solvent annealing,which indicates that the performance of polymer solar cells（PSCs）can probably be improved by improving the phase segregation and penetrative networks of donor and acceptor blends.

关 键 词：聚合物 富勒烯 表面形貌 相分离 能量转换效率 

分 类 号：O175.29[理学—数学]