热处理对半固态挤压SiC_p/2024复合材料的影响  

Effects of Heat Treatment on SiC_p/2024 Composites Prepared by Semi-solid Thixoextruding Forming

作　　者：马郁柏 阎峰云[1,2] 刘兴丹 赵红娟[1,2] 

机构地区：[1]兰州理工大学省部共建有色金属先进加工与再利用国家重点实验室 [2]兰州理工大学有色金属合金及加工教育部重点实验室

出　　处：《特种铸造及有色合金》2016年第4期422-424,共3页Special Casting & Nonferrous Alloys

摘　　要：采用扫描电镜(SEM)、X射线衍射仪(XRD)、电子探针等研究了固溶处理对半固态挤压SiC_p/2024复合材料的组织和性能的影响。结果表明,SiCp/2024复合材料经过500℃×12h固溶和170℃×16h时效处理后,抗拉强度达到了478MPa,硬度(HV)为150,而在未热处理之前材料硬度(HV)仅为86,抗拉强度也只有350 MPa。Effects of heat treatment on microstructure and properties of SiCp/2024 composites prepared by semi-solid thixo-extruding forming were investigated by scanning electron microscopy（SEM）,X-ray diffraction（XRD）and electron probe.The experimental results show that with solid solution at 500℃for12hand aging treatment at 170℃for 16 h,tensile strength and hardness of SiCp/2024 composites reach478 MPa and 150 HV,respectively,while these reach 350 MPa and 86 HV,respectively,before heat treatment.

关 键 词：SICP/2024复合材料 固溶温度 时效温度 力学性能 

分 类 号：TB33[一般工业技术—材料科学与工程]