高频电阻焊管纵焊缝泄漏原因分析  

Analysis on Reasons for Leakage of Longitudinal Weld Seam for HFW Pipe

作　　者：王高峰[1,2] 张珂[3] 陆璟[4] 刘迎来[1,2] 聂向晖[1,2] 赵金兰[1,2] 王长安[1,2] 许彦[1,2] 艾志刚[1,2] 

机构地区：[1]中国石油集团石油管工程技术研究院,陕西西安710077 [2]北京隆盛泰科石油管科技有限公司,北京100101 [3]中航工业西安飞行自动控制研究所,陕西西安710065 [4]中国石化销售有限公司华东分公司,浙江杭州310002

出　　处：《热加工工艺》2016年第9期255-258,共4页Hot Working Technology

摘　　要：某燃气管道工程用高频电阻焊管在现场进行投产前水压密封试验时,发生泄漏,通过宏观分析、化学分析、力学性能检测、金相观察、扫描电镜及能谱分析,对该钢管的泄漏原因进行了分析。结果表明,由于钢管焊缝中存有灰斑缺陷,导致该钢管试压时纵焊缝开裂。最后提出几点避免灰斑缺陷的建议,以供生产时参考。HFW pipes used for gas pipeline projects before using were leaked during hydraulic seal test in worksite. The reasons for the leak of steel were analyzed by macro-examination, chemical composition analysis, mechanical test, OM, SEM and EDS analysis. The results show that because of the gray spot defects existing in weld seam, the longitudinal weld seam of the steels fractures during the hydraulic seal test. Then, some suggestions are provided to avoid the gray spot, which can be used as the references for HFW pipe production.

关 键 词：高频电阻焊管 开裂 灰斑 

分 类 号：TG452[金属学及工艺—焊接] TG457.6