Preparation of manganese sulfate from low-grade manganese carbonate ores by sulfuric acid leaching  

作　　者：Qing-quan Lin Guo-hua Gu Hui Wang Ren-feng Zhu You-cai Liu Jian-gang Fu 

机构地区：[1]School of Minerals Processing and Bioengineering, Central South University [2]School of Chemistry and Chemical Engineering, Central South University

出　　处：《International Journal of Minerals,Metallurgy and Materials》2016年第5期491-500,共10页矿物冶金与材料学报（英文版）

基　　金：supported by the National Natural Science Foundation of China (51374249)

摘　　要：In this study, a method for preparing pure manganese sulfate from low-grade ores with a granule mean size of 0.47 mm by direct acid leaching was developed. The effects of the types of leaching agents, sulfitric acid concentration, reaction temperature, and agitation rate on the leaching efficiency of manganese were investigated. We observed that sulfuric acid used as a leaching agent provides a similar leach- ing efficiency of manganese and superior selectivity against calcium compared to hydrochloric acid. The optimal leaching conditions in sul- furic acid media were determined; under the optimal conditions, the leaching efficiencies of Mn and Ca were 92.42% and 9.61%, respec- tively. Moreover, the kinetics of manganese leaching indicated that the leaching follows the diffusion-controlled model with an apparent ac- tivation energy of 12.28 kJ·mol-l. The purification conditions of the leaching solution were also discussed. The results show that manganese dioxide is a suitable oxidant of ferrous ions and sodium dimethyldithiocarbamate is an effective precipitant of heavy metals. Finally, through chemical analysis and X-ray diffraction analysis, the obtained product was determined to contain 98% of MnSOa4·H20.In this study, a method for preparing pure manganese sulfate from low-grade ores with a granule mean size of 0.47 mm by direct acid leaching was developed. The effects of the types of leaching agents, sulfitric acid concentration, reaction temperature, and agitation rate on the leaching efficiency of manganese were investigated. We observed that sulfuric acid used as a leaching agent provides a similar leach- ing efficiency of manganese and superior selectivity against calcium compared to hydrochloric acid. The optimal leaching conditions in sul- furic acid media were determined; under the optimal conditions, the leaching efficiencies of Mn and Ca were 92.42% and 9.61%, respec- tively. Moreover, the kinetics of manganese leaching indicated that the leaching follows the diffusion-controlled model with an apparent ac- tivation energy of 12.28 kJ·mol-l. The purification conditions of the leaching solution were also discussed. The results show that manganese dioxide is a suitable oxidant of ferrous ions and sodium dimethyldithiocarbamate is an effective precipitant of heavy metals. Finally, through chemical analysis and X-ray diffraction analysis, the obtained product was determined to contain 98% of MnSOa4·H20.

关 键 词：manganese ore treamaent manganese carbonate LEACHING leaching kinetics manganese sulfate 