Hydrothermal synthesis of blue-emitting YPO4：Yb3＋ nanophosphor  

作　　者：Guangfa WANG Linhui GAO Hongliang ZHU Weijie ZHOU 

机构地区：[1]College of Materials and Textiles, Zhejiang Sci-Tech University, Hangzhou 310018, China

出　　处：《Frontiers of Materials Science》2016年第2期197-202,共6页材料学前沿（英文版）

摘　　要：The blue-emitting YPO4 phosphors doped with Yb3＋ were prepared by a simple hydrothermal method. All the products were characterized by XRD and TEM, which revealed that they were zircon structure with leaf-like morphology. According to the analysis of photoluminescence spectra, upon ultraviolet （275 nm） excitation, the Yb3＋ doped YPO4 phosphor showed an intense blue emission composed of two main bands at 420 and 620 nm assigned to charge transfer state （CTS） → 2Fs/2 and CTS →ZF7/2, respectively. Moreover, the optimum doping concentration of Yb3＋ in YPO4 phosphor was 1%, which exhibited the maximum emission intensity. The possible physical mechanism of concentration quenching was discussed, and the critical transfer distance determined to be 23.889 A. In particular, the color purity of the as-synthesized Yb3＋ doped YPO4 phosphor was as high as 83%, which made it an excellent candidate for blue-emitting materials.The blue-emitting YPO4 phosphors doped with Yb3＋ were prepared by a simple hydrothermal method. All the products were characterized by XRD and TEM, which revealed that they were zircon structure with leaf-like morphology. According to the analysis of photoluminescence spectra, upon ultraviolet （275 nm） excitation, the Yb3＋ doped YPO4 phosphor showed an intense blue emission composed of two main bands at 420 and 620 nm assigned to charge transfer state （CTS） → 2Fs/2 and CTS →ZF7/2, respectively. Moreover, the optimum doping concentration of Yb3＋ in YPO4 phosphor was 1%, which exhibited the maximum emission intensity. The possible physical mechanism of concentration quenching was discussed, and the critical transfer distance determined to be 23.889 A. In particular, the color purity of the as-synthesized Yb3＋ doped YPO4 phosphor was as high as 83%, which made it an excellent candidate for blue-emitting materials.

关 键 词：blue-emitting nanophosphors hydrothermal synthesis luminescence Yb3＋ doped YPO4 

分 类 号：TN383.1[电子电信—物理电子学] TQ171.112[化学工程—玻璃工业]