马来酸酐接枝三元乙丙橡胶共聚物增容AES/PC共混物的研究  

Research of AES/PC Blends Compatibilized by EPDM-g-MAH Copolymer

作　　者：苏鹏[1] 邹晓轩[1] 杨家富[1] 敬波[1] 戴文利[1] 

机构地区：[1]湘潭大学化学学院,湖南湘潭411105

出　　处：《中国塑料》2016年第5期50-54,共5页China Plastics

摘　　要：研究了马来酸酐接枝三元乙丙橡胶共聚物(EPDM-g-MAH)作为增容剂对丙烯腈-三元乙丙橡胶-苯乙烯共聚物/聚碳酸酯(AES/PC)(70/30)共混物结构和性能的影响。结果表明,EPDM-g-MAH作为反应型增容剂,能有效地减小低橡胶含量的AES/PC共混物中PC分散相的粒径,提高共混物的力学性能;当EPDM-g-MAH用量为3份时,橡胶含量为21%的AES/PC共混物的缺口冲击强度提高近1倍,同时能保持较高的拉伸强度和热变形温度。Maleic anhydride grafted EPDM （EPDM-g-MAH） was used as a compatibilizer for AES/ PC （70 = 30） blends. When the rubber content in AES/PC blends was 10w, EPDM-g-MAH could reduce the size of the dispersed particle phase. When the dosage of EPDM-g-MAH was 3 phr and the rubber content of AES/PC blends was 21%, the blends would maintain high tensile strength and high heat distortion temperature, while the notched impact strength will be nearly double.

关 键 词：丙烯腈-三元乙丙橡胶-苯乙烯共聚物 聚碳酸酯 反应性增容 相形态 

分 类 号：TQ317[化学工程—高聚物工业]