Evolution of Microstructure and Ordering in Rolling Process of Fe-6. 5 mass% Si Alloy  

作　　者：Hui LI Yong-feng LIANG Feng YE 

机构地区：[1]State Key Laboratory for Advanced Metals and Materials,University of Science and Technology Beijing

出　　处：《Journal of Iron and Steel Research International》2016年第5期453-458,共6页

基　　金：Item Sponsored by Major State Basic Research Development Program of China(2011CB606304);High-tech Research and Development Program of China(2012AA03A505);National Natural Science Foundation of China(51301019,51471031)

摘　　要：Fe-6. 5 mass% Si alloy is an excellent soft magnetic material with good application prospects. After rolling,the structure of the sheet is likely to be heterogeneous along the normal direction. The microstructure and ordering evolution in the thickness range of the sheets during hot-warm rolling process was studied by means of optical microscope and transmission electron microscope. The results show that dynamic recrystallization occurs in the surface parts during the hot and warm rolling processes,where the grains are equiaxed but have high density of dislocations due to the large deformation. The grains in the center part are elongated along the rolling direction. It is also found that in the hot rolled sheet,the center part has lower density of dislocations because of dynamic recovery. Meanwhile,this part has higher ordering content compared with the surface part,indicating that the high density of dislocations can inhibit the formation of ordering in the air cooling process after hot rolling. In the warm rolling process,both of the parts are deformed heavily. Large deformation destroys ordered phases and induces disordering. The ordering content is low in the whole warm rolled sheet.Fe-6. 5 mass% Si alloy is an excellent soft magnetic material with good application prospects. After rolling,the structure of the sheet is likely to be heterogeneous along the normal direction. The microstructure and ordering evolution in the thickness range of the sheets during hot-warm rolling process was studied by means of optical microscope and transmission electron microscope. The results show that dynamic recrystallization occurs in the surface parts during the hot and warm rolling processes,where the grains are equiaxed but have high density of dislocations due to the large deformation. The grains in the center part are elongated along the rolling direction. It is also found that in the hot rolled sheet,the center part has lower density of dislocations because of dynamic recovery. Meanwhile,this part has higher ordering content compared with the surface part,indicating that the high density of dislocations can inhibit the formation of ordering in the air cooling process after hot rolling. In the warm rolling process,both of the parts are deformed heavily. Large deformation destroys ordered phases and induces disordering. The ordering content is low in the whole warm rolled sheet.

关 键 词：rolling process microstructure ordering Fe-6.5 mass% Si alloy 

分 类 号：TG335[金属学及工艺—金属压力加工]