时效处理对铝锂合金断裂行为的影响  

Effect of Aging Treatment on Fracture Behavior of Al-Li Alloy

作　　者：温培刚[1] 李国爱[1] 陆政[1] 赵亮亮[1] 

机构地区：[1]北京航空材料研究院,北京100083

出　　处：《失效分析与预防》2016年第3期139-142,167,共5页Failure Analysis and Prevention

基　　金：国家自然科学基金(51474195)

摘　　要：通过拉伸试验机、扫描电镜、透射电镜等设备对不同时效工艺下铝锂合金厚板的拉伸性能、微观组织以及断裂特征进行了系统研究。结果表明:随人工时效时间延长,合金的高向强度迅速增加,同时延伸率快速降低,合金的断裂方式也由穿晶滑移剪切+沿晶混合断口转变为单纯的沿晶断口。时效过程中晶内析出了大量的T_1相,提高了晶内强度,抑制了拉伸过程中晶内的协调变形,降低了合金的塑性并导致合金沿晶开裂。Effect of aging treatment on the tensile properties, microstructure and fracture characteristics of A1-Li alloy werestudied by tensile testing,SEM ad TEM. The results show that,with the increase of aging time,the strength of short-transverse direction increases quickly and the elongation decreases rapidly. The fracture mode changes from tintergranular cracking to intergranular cracking. Abundant T1 phase precipitates in grains during aging process,which enhancesthe strength and restraining the matching deformation within grain,leading to intergranular

关 键 词：铝锂合金 断裂特征 T1析出相 人工时效 拉伸性能 

分 类 号：TG146.2[一般工业技术—材料科学与工程]