绝缘导热加成型有机硅灌封胶的制备及性能研究  

Preparation and Properties of Electrical Insulated and Thermal Conductive Addition-Cure Silicone Encapsulant

作　　者：潘科学[1] 赖学军[1] 李红强[1] 胡新嵩 曾幸荣[1] 

机构地区：[1]华南理工大学材料科学与工程学院,广东广州510450 [2]广州市高士实业有限公司,广东广州510640

出　　处：《橡胶工业》2016年第6期347-351,共5页China Rubber Industry

基　　金：粤港关键领域重点突破项目(2008A092000002)

摘　　要：研究绝缘导热加成型有机硅灌封胶的制备及性能。结果表明:当采用粘度为300和1 000 m Pa·s的端乙烯基硅油以质量比40∶60复配、选用活性氢质量分数为0.005 0的含氢硅油且硅氢基/硅乙烯基摩尔比为1.2时,有机硅灌封胶的物理性能较佳;当三氧化二铝用量为150份时,有机硅灌封胶具有良好的综合性能。In this study,the electrical insulating and thermal conductive addition-cure silicone encapsulant was prepared and its properties were investigated. The results showed that,when the mass ratio of vinyl end silicone oils with viscosity of 300 and 1 000 m Pa·s was 40∶60,active hydrogen mass fraction of hydrogen-containing silicone oil was 0. 005 0 and molar ratio of Si H and Si Vi was 1. 2,the physical properties of silicone encapsulant were good. When the addition level of Al2O3 was 150 phr,the silicone encapsulant had good comprehensive performance.

关 键 词：有机硅灌封胶 加成型 绝缘 导热 

分 类 号：TQ333.93[化学工程—橡胶工业] TQ336.42