机械部件表面Ni/Al_2O_3熔覆层的制备与性能分析  

Preparation and Properties of Ni/Al_2O_3 Cladding Layer on Mechanical Part

作　　者：钱灿荣[1] 

机构地区：[1]肇庆学院电子信息与机械工程学院,广东肇庆526061

出　　处：《铸造技术》2016年第6期1144-1145,1149,共3页Foundry Technology

摘　　要：通过对不同加热温度和保温时间下熔覆层制备工艺参数进行实验研究,确定了机械部件ZG45表面Ni/Al_2O_3熔覆层制备的最佳工艺参数。结果表明,在1 050℃下加热1 h,Ni/Al_2O_3熔覆层与母材ZG45的结合程度良好。在细晶强化、弥散强化和Cr_7C_3硬质强化的共同作用下,从母材到熔覆层表面的硬度逐渐升高。The optimal process for preparing Ni/Al2O3 cladding layer on mechanical part of ZG45 was studied by cladding at different temperatures and holding times. The results show that the bonding strength between Ni/Al2O3 cladding layer and matrix ZG45 is the best at 1 050 ℃ for 1 h. The hardness of the cladding layer gradually increase from matrix to the cladding surface due to fine grain strengthening, dispersion strengthening and Cr7C3 stereoplasm strengthen.

关 键 词：机械部件 熔覆层 性能 