单晶合金(NiCoCrAlYHf+AlYSi)复合涂层抗氧化性能研究  

Study of oxidation resistance composite coatings on single crystal super alloy

作　　者：蔡妍[1] 李建平[1] 刘玉琢[1] 何利民[1] 牟仁德[1] 

机构地区：[1]北京航空材料研究院,北京100095

出　　处：《真空》2016年第3期1-6,共6页Vacuum

基　　金：国家863项目(2015AA034403)

摘　　要：本文采用真空电弧镀技术(AIP)在DD9单晶高温合金基体上沉积60μm^80μm复合涂层(NiCoCrAlYHf+AlYSi),分析了复合涂层的组织及结构。对于沉积复合涂层的试样进行了1150℃循环抗氧化实验,来评价其抗氧化性能,通过扫描电镜(SEM)分析氧化前后的试样显微形貌,用X-射线衍射仪分析涂层的相结构,通过氧化速率对涂层抗氧化性能进行表征。试验结果表明:复合涂层明显改善了合金的抗高温氧化性能;1150℃循环氧化条件下,复合涂层寿命大于4200h。Composite coatings（NiCoCrAlYHf＋AlYSi）was deposited on DD9 nickel based single crystal super-alloy substrate by arc ion plating（AIP）. The high temperature oxidation behavior at 1150℃ was studied. The coatings were characterized by scanning electron microscopy and X-ray diffraction. The results indicate that the composite coatings can improve the high temperature oxidation resistance of DD9 super-alloy. The lifetime of the composite coatings is over 4200 h for high temperature oxidation in air at 1150℃.

关 键 词：(NiCoCrAlYHf+AlYSi)复合涂层 单晶高温合金 抗高温氧化性能 电弧离子镀 

分 类 号：TG174.4[金属学及工艺—金属表面处理] TB43[金属学及工艺—金属学]