铜/金刚石复合材料电磁轨道烧蚀特性的实验研究  

Experimental Study of Cu/Diamond Composite Electromagnetic Rail Ablation Characteristics

作　　者：曹海要 战再吉[1] 

机构地区：[1]燕山大学亚稳材料制备技术与科学国家重点实验室,河北秦皇岛066004

出　　处：《高压物理学报》2016年第4期317-322,共6页Chinese Journal of High Pressure Physics

基　　金：国家重点基础研究发展计划(973计划)资助项目(2010CB731600)

摘　　要：通过对电磁轨道发射初期阶段,铜/金刚石复合材料轨道在预紧力0.4-2.0kN、电流100-300kA下的滑动电烧蚀实验分析发现：由于受到焦耳热及电弧热的双重作用,铜/金刚石复合材料的质量损失、烧蚀深度随电流的增大而呈现增加趋势,随预紧力的增加而呈下降趋势;在主烧蚀区域形成凹凸不平的形貌,由于部分金刚石的脱落形成一定数量的微孔,在强交变温度场作用下产生了热应力裂纹;在烧蚀区域的边缘,主要由于熔融液态金属受强电磁场涡流的作用而形成微凸及飞溅形貌;在滑动电接触区域则表现为电枢微凸体与轨道之间摩擦形成的划痕,其磨损机制为磨粒磨损;在铜/金刚石复合材料主烧蚀区的横截面,由于轨道材料的长高比过大而造成散热速率的不同,形成不同尺度的晶粒组织,表面硬度下降较大。In the present work we investigated the ablation behavior of the Cu/diamond composite material under the current ranging from 100 to 300kA and the preload ranging from 0.4to 2.0kN in the initial stage of the electromagnetic rail launch.The analysis reveals that,due to the dual function of the joule heat and electric arc heat,the mass loss and the ablation depth of Cu/diamond composite increase with the increase of the current and decrease with the increase of the preload;in the main ablation area,uneven topography is formed,and the exfoliation of the second phase particles causes a certain number of micro-pores,and thermal stress cracks are produced due to the strong alternating temperature field;micro-bulges and splash at the edge of the main ablation area are attributed to the molten liquid metal affected by the strong eddy current electromagnetic field;in the electrical sliding contact area,micro-scratches are formed due to the friction between the micro-bulges on the armature and the rail,and its wear mechanism is the abrasive wear;in the cross section of the ablation area of Cu/diamond composite,different scales of grains are formed corresponding to the different cooling rates resulting from the rails large length-height ratio,and the surface hardness of Cu/diamond composite undergoes a considerable decrease.

关 键 词：电磁轨道发射 铜/金刚石复合材料 电流 预紧力 烧蚀 

分 类 号：O442[理学—电磁学] TG146.1[理学—物理]