热处理制度对TC9钛合金棒材组织和力学性能的影响  

Effect of Heat Treatment on Microstructure and Properties of TC9 Titanium Alloy Bars

作　　者：关蕾 陶海林 雒水会 蒋纪新 

机构地区：宝鸡钛业股份有限公司,陕西宝鸡721014

出　　处：《世界有色金属》2016年第7期44-46,共3页World Nonferrous Metals

摘　　要：通过采用不同的热处理制度,研究了双重退火温度对TC9钛合金棒材显微组织、室温拉伸性能、高温拉伸性能和热稳定性能的影响。研究结果表明：随着一次退火温度的升高,β相明显增多,初生α相数量急剧减少;随着二次退火温度的升高,显微组织变化不大。TC9钛合金采用960℃/1.5h,AC＋530℃/6h,AC的双重退火工艺时,可得到较高的室温强度,高温强度（500℃）和热稳定性（500℃,100h）也达到良好匹配。The effects of different heat treatment processes on the microstructure and properties of TC9 titanium alloy bars were studied. The results show that： with first annealing temperature increasing, the content of β-phase increases, while the content of primary α-phase decreases; with the second annealing temperature increasing, the microstructure of TC9 titanium alloy change a little. Better room-temperature strength of TC9 titanium alloy can be got by using double annealing： 960℃ /1.5h, AC＋530℃ /6h, AC. The high-temperature strength（500℃） and thermal stability properties（500℃, 100h） can reach a good match.

关 键 词：TC9钛合金 双重退火 组织 力学性能 

分 类 号：TG166.5[金属学及工艺—热处理]