Study on Composite Ceramic Coating Prepared by Self-propagating High Temperature Synthesis and Pseudo Hot Isostatic Pressing

作　　者：程勇[1] 苏勋家[1] 侯根良[1] 杨权[2] 

机构地区：[1]第二炮兵工程大学,陕西西安710025 [2]武汉军械士官学校特种车辆教研室,湖北武汉430075

出　　处：《热加工工艺》2016年第16期130-132,共3页Hot Working Technology

基　　金：陕西省科技创新团队资助项目(2014KCT-03)

摘　　要：采用自蔓延高温合成和使用HfC陶瓷粉末的准热等静压技术制备了致密ZrC陶瓷材料及复合陶瓷涂层。使用XRD、SEM等仪器对涂层的物相与组织形貌进行了分析。结果表明:复合涂层主要由大块的HfC颗粒和细小的ZrC晶粒组成。它是由HfC粉末空隙的ZrC晶粒与HfC粉末冶金结合形成的。涂层整体致密,孔隙率低;热震试验显示涂层具有良好的结合力。Dense ZrC ceramic material and the composite ceramic coating were prepared by self-propagating high temperature synthesis and pseudo hot isostatic pressing using HfC ceramic powder. The phases and microstructure of the coating were analyzed by XRD, SEM. The results show that the composite coating is mainly composed of bulk HfC particles and fine ZrC grains. The coating is formed by the metallurgy combination of ZrC grains in the void of HfC powder and HfC powder. The coating is dense with low porosity, and it has good bonding strength shown by the thermal shock test.

关 键 词：自蔓延高温合成 准热等静压 涂层 陶瓷 ZRC HFC 

分 类 号：TB35[一般工业技术—材料科学与工程] TG174[金属学及工艺—金属表面处理]