高铝硅酸盐玻璃对耐火材料的侵蚀  

Refractory Erosion by High Aluminum Silicate Glass

作　　者：周莉 赵会峰 姜宏[1,2] 

机构地区：[1]海南中航特玻科技有限公司,海南澄迈571924 [2]海南省特种玻璃重点实验室,海南大学,海南海口570100

出　　处：《材料科学与工程学报》2016年第4期634-637,共4页Journal of Materials Science and Engineering

基　　金：国家科技支撑计划资助项目(2013BAE03B02);海南省重大科技资助项目(ZDZX2013002)

摘　　要：运用静态实验的方法,以高铝硅酸盐玻璃及配合料为熔体,对耐火材料进行侵蚀实验。对侵蚀前后的耐火材料进行研究,探讨了高温下高铝硅酸盐玻璃及碱蒸汽对耐火材料的侵蚀机理。实验结果表明:高锆砖抗铝硅玻璃液侵蚀性最好;αβ刚玉砖和β刚玉砖抗碱蒸汽侵蚀性最好。In order to study refractory erosion behavior, static experiments were carried out on the erosion of various kinds of refractory by high aluminum silicate cullet and glass batch melts By comparing the morphology of the refractory before and after the erosion experiments, the mechanisms of the erosions by the aluminum silicate glass and by the alkali vapor out of the refractory at the high temperature werer discussed. The experimental results show that： the erosion resistance of high zirconia brick to aluminosilicate glass is the best, while the erosion resistance of αβ and β corundum bricks to alkali vapor is also the best.

关 键 词：高铝硅酸盐玻璃 耐火材料 侵蚀 

分 类 号：TQ171.718.2[化学工程—玻璃工业]