Synthesis and Characterization of Crystallizable Aliphatic Thermoplastic Poly(ester urethane) Elastomers through a Non-isocyanate Route  

作　　者：Yue Li Su-qing Li 赵京波 Zhi-yuan Zhang Jun-ying Zhang Wan-tai Yang 

机构地区：[1]Key Laboratory of Carbon Fiber and Functional Polymers(Beijing University of Chemical Technology),Ministry of Education [2]State Key Laboratory of Chemical Resource Engineering,College of Materials Science and Engineering,Beijing University of Chemical Technology,Beijing 100029,China

出　　处：《Chinese Journal of Polymer Science》2016年第10期1220-1233,共14页高分子科学（英文版）

基　　金：financially supported by the National Natural Science Foundation of China(Nos.21244006 and 50873013)

摘　　要：A simple non-isocyanate route is developed for synthesizing crystallizable aliphatic thermoplastic poly（ester urethane） elastomers （TPEURs） with good thermal and mechanical properties. Three prepolymers of 1,6-bis（hydroxyethyloxycarbonylamino） hexane （BHCH）, i.e. PrePBHCHs, were prepared through the self-transurethane polycondensation of BHCH. A poly（butylene adipate） prepolymer （PrePBA） with terminal HO-- groups was prepared and used as a polyester glycol. A series of TPEURs were prepared by the co-polycondensation of the PrePBHCHs with PrePBA at 170 ℃under a reduced pressure of 399 Pa. The TPEURs were characterized by gel permeation chromatography, FTIR, 1H-NMR, differential scanning calorimetry, thermogravimetric analysis, wide-angle X-ray diffraction, atomic force microscopy, and tensile test. The TPEURs exhibited Mn up to 23300 g/mol, Mw up to 51100 g/mol, Tg ranging from -33.8 ℃ to -3.1 ℃, Tm from 94.3 ℃ to 111.9 ℃, initial decomposition temperature over 274.7℃, tensile strength up to18.8 MPa with a strain at break of 450.0%, and resilience up to 77.5%. TPU elastomers with good crystallization and mechanical properties were obtained through a non-isocyanate route.A simple non-isocyanate route is developed for synthesizing crystallizable aliphatic thermoplastic poly（ester urethane） elastomers （TPEURs） with good thermal and mechanical properties. Three prepolymers of 1,6-bis（hydroxyethyloxycarbonylamino） hexane （BHCH）, i.e. PrePBHCHs, were prepared through the self-transurethane polycondensation of BHCH. A poly（butylene adipate） prepolymer （PrePBA） with terminal HO-- groups was prepared and used as a polyester glycol. A series of TPEURs were prepared by the co-polycondensation of the PrePBHCHs with PrePBA at 170 ℃under a reduced pressure of 399 Pa. The TPEURs were characterized by gel permeation chromatography, FTIR, 1H-NMR, differential scanning calorimetry, thermogravimetric analysis, wide-angle X-ray diffraction, atomic force microscopy, and tensile test. The TPEURs exhibited Mn up to 23300 g/mol, Mw up to 51100 g/mol, Tg ranging from -33.8 ℃ to -3.1 ℃, Tm from 94.3 ℃ to 111.9 ℃, initial decomposition temperature over 274.7℃, tensile strength up to18.8 MPa with a strain at break of 450.0%, and resilience up to 77.5%. TPU elastomers with good crystallization and mechanical properties were obtained through a non-isocyanate route.

关 键 词：Non-isocyanate route Thermoplastic polyurethane elastomers Diurethanediol Transurethane polycondensation Poly（ester urethane）s. 

分 类 号：TQ334.1[化学工程—橡胶工业]