冷却速度对2D-C_f/Mg复合材料性能的影响  

Effect of Cooling Rate on Performance of 2D-C_f/Mg Composites

作　　者：卫新亮[1] 齐乐华[1] 苏常青[1] 张婷[1] 

机构地区：[1]西北工业大学机电学院

出　　处：《特种铸造及有色合金》2016年第9期897-900,共4页Special Casting & Nonferrous Alloys

基　　金：国家自然科学基金资助项目(51275417;51521061);国家高技术研究发展计划(863计划)资助项目(2015AA8011004B)

摘　　要：采用真空吸渗挤压工艺制备二维连续碳纤维增强镁基(2D-C_f/Mg)复合材料,研究了不同冷却速度下C_f/Mg复合材料中的碳纤维表面形貌、复合材料的硬度和拉伸强度。试验结果表明,较高的冷却速度可降低C_f/Mg复合材料的界面反应程度,减少碳纤维的表面损伤,有助于复合材料的硬度和强度提高。制备的T700碳纤维增强2D-C_f/Mg复合材料的抗拉强度可达450 MPa。2dimension-continuous carbon fiber reinforced magnesium（2D-Cf/Mg）composites were fabricated by liquid-solid extrusion directly combining with vacuum infiltration technique.The effects of different cooling rate on the carbon fiber,hardness and ultimate tensile strength of Cf/Mg composites were analyzed.The experimental results reveal that a higher cooling rate can reduce the damage of carbon fiber,relief the interface reaction,and improve the ultimate tensile strength（UTS）and hardness of the composites prepared.The tensile strength of 2D-Cf/Mg composites with T700 carbon fiber can reach 450 MPa.

关 键 词：真空吸渗挤压 冷却速度 Cf/Mg复合材料 

分 类 号：TB33[一般工业技术—材料科学与工程]