Process improvement in laser hot wire cladding for martensitic stainless steel based on the Taguchi method  

作　　者：Zilin HUANG Gang WANG Shaopeng WEI Changhong LI Yiming RONG 

机构地区：[1]School of Mechanical, Electronic and Control Engineering, Beijing Jiaotong University, Beijing 100044, China [2]Beijing Key Laboratory of Precision/Ultra-precision Manufacturing Equipments and Control,Tsinghua University, Beijing 100084, China [3]Mechanical and Energy Engineering Department, South University of Science and Technology of China, Shenzhen 518055, China

出　　处：《Frontiers of Mechanical Engineering》2016年第3期242-249,共8页机械工程前沿（英文版）

摘　　要：Laser hot wire cladding, with the prominent features of low heat input, high energy efficiency, and high precision, is widely used for remanufacturing metal parts. The cladding process, however, needs to be improved by using a quantitative method. In this work, volumetric defect ratio was proposed as the criterion to describe the integrity of forming quality for cladding layers. Laser deposition experiments with FV520B, one of martensitic stainless steels, were designed by using the Taguchi method. Four process variables, namely, laser power （P）, scanning speed （Vs）, wire feed rate （Vf）, and wire current （/）, were optimized based on the analysis of signal-to-noise （S/N） ratio. Metallurgic observation of cladding layer was conducted to compare the forming quality and to validate the analysis method. A stable and continuous process with the optimum parameter combination produced uniform microstructure with minimal defects and cracks, which resulted in a good metallurgical bonding interface.Laser hot wire cladding, with the prominent features of low heat input, high energy efficiency, and high precision, is widely used for remanufacturing metal parts. The cladding process, however, needs to be improved by using a quantitative method. In this work, volumetric defect ratio was proposed as the criterion to describe the integrity of forming quality for cladding layers. Laser deposition experiments with FV520B, one of martensitic stainless steels, were designed by using the Taguchi method. Four process variables, namely, laser power （P）, scanning speed （Vs）, wire feed rate （Vf）, and wire current （/）, were optimized based on the analysis of signal-to-noise （S/N） ratio. Metallurgic observation of cladding layer was conducted to compare the forming quality and to validate the analysis method. A stable and continuous process with the optimum parameter combination produced uniform microstructure with minimal defects and cracks, which resulted in a good metallurgical bonding interface.

关 键 词：process optimization Taguchi method signalto-noise （S/N） ratio volumetric defect ratio laser hot wire cladding 

分 类 号：TH[机械工程]