Influence of synthesis temperature on electrochemical performance of polyoxomolybdate as cathode material of lithium ion battery  

反应合成温度对锂离子电池正极材料聚氧钼酸盐电化学性能的影响（英文）

作　　者：李文良[1,2] 倪尔福 李新海[1] 郭华军[1] 

机构地区：[1]中南大学冶金与环境学院,长沙410083 [2]豪鹏国际集团,深圳518111

出　　处：《Transactions of Nonferrous Metals Society of China》2016年第10期2687-2692,共6页中国有色金属学报（英文版）

摘　　要：In order to improve the electrochemical performance of polyoxomolybdate Na3[AlMo6O24H6]（NAM） as the cathode material of lithium ion battery, the NAM materials with small particle size were synthesized by elevatingthe synthesistemperaturein the solution.The as-prepared NAM materials were investigated by FT-IR, XRD, SEM and EIS. Their discharge-charge and cycle performance were also tested. The resultsshowthat the particle size decreasesto less than10μm at the temperature ofhigher than 40℃.When synthesized at 80℃,the NAMwiththe smallest particle size （-3μm）exhibitsthe best electrochemical performance such ashigh initial discharge capacity of 409 mA·h/gandcoulombic efficiency of 95% in the first cycle at 0.04C.为了改善聚氧钼酸盐 Na3[AlMo6O24H6]（NAM）作为锂离子电池正极材料的电化学性能，通过升高反应溶液的温度，得到了小粒径的NAM材料，并对其进行了红外光谱、XRD、扫描电镜、EIS等分析和充放电性能测试。结果表明，当反应温度高于40℃时，粒径降低到10μm以下。当合成温度达到80℃时，NAM的粒径最小（-3μm），且其电化学性能最佳，在首次循环过程中，0.04C下的首次放电容量高达409 mA·h/g，库伦效率达95%。

关 键 词：POLYOXOMOLYBDATE lithium ion battery cathode material high capacity 

分 类 号：TM912[电气工程—电力电子与电力传动]