Effect of Ga_2O_3 on Structure and Properties of Calcium Aluminate Glasses  

作　　者：王衍行 ZU Chengkui HE Kun ZHAO Huifeng LIU Yonghua 

机构地区：[1]China Building Materials Academy, Beijing 100024, China

出　　处：《Journal of Wuhan University of Technology(Materials Science)》2016年第5期961-964,共4页武汉理工大学学报（材料科学英文版）

基　　金：Funded by the National Natural Science Foundation of China(No.60808024)

摘　　要：The effect of Ga_2O_3 on the structure and properties of calcium aluminate glasses fabricated by vacuum melting process was investigated by Raman spectrum, differential scanning calorimeter（DSC）, and infrared spectrum methods. The results show that calcium aluminate glass network only consists of [AlO_4] tetrahedral units. With the gradual addition of Ga_2O_3, the quantity of [GaO_4] tetrahedral units increases. Substitution of Ga_2O_3 for Al_2O_3 results in a decrease in Tg, Tx, and Tp, and an increase in the thermal stable index ΔT. Similarly, the absorption band around 3.0 μm obviously reduces and the transparency in 4.0-6.0 μm rapidly increases with increasing Ga_2O_3 content. However, the chemical stability of calcium aluminate glasses decreases if Ga_2O_3 is introduced due to the increasing of [GaO_4] units in the glass network.The effect of Ga_2O_3 on the structure and properties of calcium aluminate glasses fabricated by vacuum melting process was investigated by Raman spectrum, differential scanning calorimeter（DSC）, and infrared spectrum methods. The results show that calcium aluminate glass network only consists of [AlO_4] tetrahedral units. With the gradual addition of Ga_2O_3, the quantity of [GaO_4] tetrahedral units increases. Substitution of Ga_2O_3 for Al_2O_3 results in a decrease in Tg, Tx, and Tp, and an increase in the thermal stable index ΔT. Similarly, the absorption band around 3.0 μm obviously reduces and the transparency in 4.0-6.0 μm rapidly increases with increasing Ga_2O_3 content. However, the chemical stability of calcium aluminate glasses decreases if Ga_2O_3 is introduced due to the increasing of [GaO_4] units in the glass network.

关 键 词：calcium aluminate glass structure thermal property infrared property chemical stability 

分 类 号：TQ171.719[化学工程—玻璃工业]