炉石活性粉混凝土静动态韧性及耐久性  

Static-Dynamic Toughness and Durability of Reactive Powder Concrete Containing Blast Furnace Slag

作　　者：孟洁平[1] 金晓勤[1] 焦俊婷[1] 

机构地区：[1]厦门理工学院土木工程与建筑学院,厦门361024

出　　处：《硅酸盐通报》2016年第10期3471-3475,共5页Bulletin of the Chinese Ceramic Society

基　　金：福建省教育厅B类项目(JB14081);厦门市2014年科技计划高校项目(3502Z20143035)

摘　　要：本研究将活性粉混凝土中的硅灰利用水淬炉石粉取代,探讨不同炉石粉取代量添加钢纤维含量1%、2% 抗压强度变化,找出炉石取代后抗压强度可达到150MPa最佳配比,并控制流度值在200-250 m m 避免添加钢纤维有沉淀的现象发生.试验结果比较150MPa炉石活性粉混凝土的静动态韧性、及微观晶体结构的差异性.In this study,the active powder concrete silica fume powder substituted with water quenching furnace,furnace explore different substituents powder added in an amount of steel fiber content of 1%,2% compressive strength,compressive strength looking baked stone,after replacing up to 150 MPa best ratio,and controls the flow value at 200-250 mm avoid adding steel fibers precipitation phenomenon. Test results compare 150 MPa furnace slag powder concrete activity of static and dynamic toughness and microstructure differences crystal structure.

关 键 词：炉石 活性粉 混凝土 静动态 韧性 

分 类 号：TQ177[化学工程—硅酸盐工业]