K_xMnO_2的溶胶-凝胶法制备及其表征  

Sol-Gel Preparation and Characterization of K_xMnO_2

作　　者：贺平祥 刘波[1] 杨玉环[1] 邱优优 赵玖翼 刘生林[1] 蒋剑波[1] 

机构地区：[1]吉首大学化学化工学院,湖南吉首416000

出　　处：《吉首大学学报（自然科学版）》2016年第5期45-49,共5页Journal of Jishou University(Natural Sciences Edition)

基　　金：吉首大学大学生研究性学习与创新性实验项目(教通[2014]48号)

摘　　要：以KHCO3,Mn（Ac）2和柠檬酸（CA）为原料,采用溶胶-凝胶法制备含钾柠檬酸锰配合物凝胶前驱体,煅烧前驱体获得目标产物,并运用XRD,FTIR,SEM等分析手段对产物进行表征.实验结果表明,当n（Mn）∶n（CA）=1,n（K）∶n（Mn）=0.17~0.3,煅烧温度800℃时,可以获得一种结构与隐钾锰类似,含有Mn8O16隧道结构的锰基嵌钾化合物KxMnO2晶体,SEM结果显示其微观形貌表现为规则扁平状薄片.The sol-gel preparation and characterization of Mn-based K-intercalating compounds KxMnO2 were investigated.The objected materials were obtained by calcining gel precursors of K-contained manganese citrate complexes through a sol-gel route with using KHCO3,Mn（Ac）2,and citric acid（CA）as raw materials,and the products were characterized by XRD,FTIR,and SEM.The results show that a crystal of K-intercalating compound KxMnO2 can be obtained which is cryptomelane-like in structure and has the channel structure of Mn8O16,when n（Mn）∶n（CA）=1,n（K）∶n（Mn）=0.17~0.3,and the calcining temperature is 800 ℃.The SEM image shows that the particles of this crystal compound have flake-like morphologies which are regular and flat.

关 键 词：KxMnO2 锰基嵌钾化合物 溶胶-凝胶法 

分 类 号：TM912.9[电气工程—电力电子与电力传动]