钢铁件序间防锈剂的研究  

Studies on the Antirust Agent used for Iron and Steel Parts between Processes

作　　者：赵思萌[1] 郝建军[1] 崔珊[1] ZHAO Simeng HAO Jianjun CUI Shan(Shenyang Ligong University, Shenyang 110159, China)

机构地区：[1]沈阳理工大学,辽宁沈阳110159

出　　处：《电镀与精饰》2016年第11期40-42,46,共4页Plating & Finishing

摘　　要：为提高钢铁件序间防锈时间,对防锈液配方和工艺进行研究,通过实验、电化学性能测试及湿热试验等方法考察了经防锈液处理的铁片的耐蚀性能。结果表明,防锈溶液组成为150 m L/L磷酸,14 g/L氧化锌,26 g/L硝酸锌,4 g/L硝酸镍,5 g/L乙醇,20 g/L马日夫盐,10 g/L亚硝酸钠,8 g/L乌洛托品,对钢铁件的耐蚀效果最佳。The antirust fluid formulation and process were investigated in order to improve the antirust time of iron and steel parts between processes. The corrosion resistant performance of antirust treated steel was studied by electrochemical performance testand damp heat test. The results showed that antirust fluid with the composition of Ha PO4 （ 150 mL/L ）, ZnO （ 14 g/L）, Zn （ NO3 ） 2 （ 26 g/L）, Ni （ NO3 ） 2 （ 4 g/L）, C2H5OH（5 g/L）, Mn（ H2PO4 ）2 （20 g/L）, NaNO2 （ 10 g/L）, C6H12 N4 （ 8 g/L） possessed the best corrosion resistant effect.