铁素体不锈钢板材厚度方向冷轧织构演变规律  

Evolution law of cold rolling texture in thickness direction for ferrite stainless steel sheet

作　　者：贺彤[1] 杜鹃[2] 刘沿东[2] 

机构地区：[1]东北大学研究院分析测试中心,辽宁沈阳110819 [2]东北大学材料与冶金学院,辽宁沈阳110819

出　　处：《物理测试》2016年第5期17-22,共6页Physics Examination and Testing

基　　金：国家科技支撑计划项目(2012BAE04B022)资金资助

摘　　要：研究了无锡和含锡两种成分的铁素体不锈钢板材厚度方向冷轧织构的演变规律。结果表明,两种板材厚度方向织构分布都不均匀,含锡板材的不均匀程度大于无锡板材,这与两种板材热轧状态下厚度方向取向分布不均匀有密切关系。The evolution law of cold rolling texture in thickness direction for ferrite stainless steel sheet with and without tin was investigated. The results showed that the texture distribution of both sheets was not uniform in the thickness direction. The uneven degree of steel sheet with tin was higher than that one without tin, which was closely related to non-uniform orientation distribution in the thickness direction of two sheets under hot rolling conditions.

关 键 词：铁素体不锈钢 织构 X-射线衍射 

分 类 号：TG337.5[金属学及工艺—金属压力加工]