Preparation and Characterisation of Sr2CeO_4:Eu^(3+) Rare Earth Luminescent Material by High Temperature Mechano-Chemical Method  

作　　者：Xue Yang Zhongbao Shao Hongqiang Ru 

机构地区：[1]School of Materials Science and Engineering, Northeastern University [2]College of Sciences, Northeastern University

出　　处：《Journal of Materials Science & Technology》2016年第10期1066-1070,共5页材料科学技术（英文版）

摘　　要：A novel, high-temperature, mechano-chemical（HTMC） method was developed to synthesise singlephase Sr_2CeO_4：Eu^（3＋）phosphor. Phosphors were characterised by X-ray diffraction（XRD）, scanning electron microscopy（SEM）, and luminescence spectra. Compared with phosphors prepared by the traditional hightemperature solid state method and citric acid gel method, single-phase Sr_2CeO_4：Eu^（3＋）powders by using the HTMC method, with small average particle sizes of about 5 μm, a narrow size distribution range and uniform dispersion, were prepared at 800 ℃, and reached their maximum luminescent intensity at 900 ℃.Under ultraviolet excitation at 298 nm, the sample showed good luminescence with the strongest red light of 616 nm. However, Sr_2CeO_4：Eu^（3＋）was prepared at the higher temperature of 1100 ℃ by solid state method and citric acid gel method. The particle size was too large and uneven with phosphor agglomeration by high-temperature solid state method. The luminescent intensity reached a maximum for Sr_2CeO_4：Eu^（3＋）phosphor at a synthesis temperature of 1100 ℃ by using the high-temperature solid state method, and at 1200 ℃ by both citric acid gel and chemical precipitation methods. Furthermore, the advantages of the Sr_2CeO_4：Eu^（3＋）powder prepared by HTMC method were discussed compared with that prepared using traditional high-temperature solid state and citric acid gel methods.A novel, high-temperature, mechano-chemical（HTMC） method was developed to synthesise singlephase Sr_2CeO_4：Eu^（3＋）phosphor. Phosphors were characterised by X-ray diffraction（XRD）, scanning electron microscopy（SEM）, and luminescence spectra. Compared with phosphors prepared by the traditional hightemperature solid state method and citric acid gel method, single-phase Sr_2CeO_4：Eu^（3＋）powders by using the HTMC method, with small average particle sizes of about 5 μm, a narrow size distribution range and uniform dispersion, were prepared at 800 ℃, and reached their maximum luminescent intensity at 900 ℃.Under ultraviolet excitation at 298 nm, the sample showed good luminescence with the strongest red light of 616 nm. However, Sr_2CeO_4：Eu^（3＋）was prepared at the higher temperature of 1100 ℃ by solid state method and citric acid gel method. The particle size was too large and uneven with phosphor agglomeration by high-temperature solid state method. The luminescent intensity reached a maximum for Sr_2CeO_4：Eu^（3＋）phosphor at a synthesis temperature of 1100 ℃ by using the high-temperature solid state method, and at 1200 ℃ by both citric acid gel and chemical precipitation methods. Furthermore, the advantages of the Sr_2CeO_4：Eu^（3＋）powder prepared by HTMC method were discussed compared with that prepared using traditional high-temperature solid state and citric acid gel methods.

关 键 词：Sr2CeO4：Eu3＋ High-temperature mechano-chemical method High-temperature solid state method Citric acid gel method 

分 类 号：TQ422[化学工程]