以转炉尘灰制备高固体分环氧防腐涂料及其性能  

High-solid-content corrosion protective epoxy paint made with converter dust and its properties

作　　者：谢珊珊[1] 李慧[1] 郝菲[1] 梁精龙[1] 霍东兴[1] XIE Shah-shah LI Hui HAO Fei LIANG Jing-long HUO Dong-xing(Key Laboratory of Ministry of Education for Modem Metallurgy Technology, College of Metallurgy and Energy, North China University of Science and Technology, Tangshan 063009, Chin)

机构地区：[1]华北理工大学冶金与能源学院现代冶金技术教育部重点实验室,河北唐山063009

出　　处：《电镀与涂饰》2016年第22期1164-1167,共4页Electroplating & Finishing

基　　金：国家自然科学基金(51401075;51474093);河北省自然科学基金(E2016209163)

摘　　要：以转炉尘灰作为颜填料,与环氧树脂制备了高固体分防腐涂料,考察了颜基比对涂膜形貌以及性能的影响。结果表明,随颜基比增加,涂料的黏度增大,涂膜的附着力降低,耐中性盐雾和乙酸盐雾的性能先增强后降低。当颜基比小于等于1.0时,涂膜平整致密,但到1.4时表面会出现缩孔。当颜基比为1.0时,涂膜的综合性能最佳。A high-solid-content corrosion protective paint was prepared from epoxy resin using converter dust as pigment and filler. The effect of pigment-to-binder ratio on the morphology and properties of its film was studied. The results showed that with the increasing of pigment-to-binder ratio, the viscosity of the paint is ＇increased, the adhesion of the film obtained from the paint is decreased, and its resistance to neutral and acetic acid salt spray corrosion is increased initially and then decreased. When the pigment-to-binder ratio is not higher than 1.0, the film obtained is levelled and compact; when it is up to 1.4, cratering is emerged on film surface. The film prepared with a pigment-to-binder ratio of 1.0 has the optimal comprehensive performance.

关 键 词：转炉尘灰 环氧树脂 高固体分涂料 颜基比 耐蚀性 盐雾试验 