Research on the Behavior of Impurity Elements in the Oxygen-rich Topblowing Smelting Reduction Process of Ilmenite

作　　者：刘艺琴[1,2] 王华[1] 卿山[1] 张爱敏[3] 郈雅丽 

机构地区：[1]昆明理工大学冶金与能源工程学院省部共建复杂有色金属资源清洁利用国家重点实验室,昆明650093 [2]云南开放大学传媒与信息工程学院,昆明650093 [3]昆明贵金属研究所,昆明650093

出　　处：《材料导报（纳米与新材料专辑）》2016年第2期396-400,共5页

基　　金：国家自然科学基金(51064015)

摘　　要：采用富氧顶吹熔融还原炼铁技术冶炼全钛铁矿,研究了温度、碱度、配碳比对铁水磷含量、硫含量及碳含量的影响。试验结果表明:在碱度为1.3、配碳比为1.0、温度由1450℃提高到1600℃时,生铁中磷含量由0.015%提高到0.021%,硫含量由0.30%降低到0.24%,碳含量变化甚微;在温度为1550℃、配碳比为1.0、碱度由0.7提高到1.5时,磷含量由0.029%降低到0.017%,硫含量由0.32%降低到0.25%,碳含量呈现先降后升的趋势,在碱度为1.2时最低,为0.8%;在温度为1550℃、碱度为1.3,随着配碳比值由0.8升高到1.2时,磷含量由0.012%升高到0.018%,硫含量则由0.21%升高到0.31%。在富氧顶吹的强氧化性气氛下,生铁中硫含量高达0.30%左右,不满足炼钢铁水要求,所以炉外脱硫对于熔融还原铁水是必要的。Adopting the iron-making process of oxygen-rich top-blowning smelting reduction from ilmenite, the effects of temperature, alkalinity and carbon fitting ratio on the phosphorus content, sulfur content and carbon content in molten iron were studied. The experimental results show that as temperature increases from 1450 ℃ to 1600 ℃, phosphorus content in the pig iron increases from 0. 015%to 0. 021%, sulfur content from 0.30% to 0. 24% and carbon content changes slightly under the conditions of basicity R of 1.3, carbon addition amount of 1.0. As basicity increases from 0.7 to 1.5, phosphorus content in the pig iron decreases from 0. 029% to 0. 017%, sulfur content from 0. 32% to 0. 25% and carbon content increases firstly, then decreases under the conditions of reduction temperature of 1550 ℃, carbon addition amount of 1.0. As carbon addition amount increases from 0. 8 to 1.2, phosphorus content in the pig iron increases from 0. 012% to 0. 018%, sulfur content from 0. 21% to 0.31% under the conditions of reduc- tion temperature of 1550 ℃, basicity R of 1.3. Sulfur content in pig iron is as high as about 0.30% for the powerful oxidization potential, which could not meet the quality of steelmaking. Therefore, it is necessary to carry out external desulfurization of pig iron.

关 键 词：熔融还原 钛铁矿 脱硫 脱磷 

分 类 号：TF557[冶金工程—钢铁冶金]