碳酸钙晶须对碱激发高炉矿渣保温材料性能的影响  被引量:1

Effect of Calcium Carbonate Whisker on the Properties of Thermal Insulation Material with Alkali Activated Blast Furnace Slag

在线阅读下载全文

作  者:邢军[1] 胡世强[1] 赵英良[1] 李浩[1] 邱景平[1] 孙晓刚[1] 

机构地区:[1]东北大学资源与土木工程学院,辽宁沈阳110819

出  处:《金属矿山》2016年第11期184-188,共5页Metal Mine

基  金:"十二五"国家科技支撑计划项目(编号:2012BAJ17B01;2012BAJ17B02)

摘  要:以高炉矿渣为主要原料,氢氧化钠为碱激发剂,双氧水为发泡剂,碳酸钙晶须为改性剂制备新型无机保温材料。探讨了碳酸钙晶须掺量对所制取保温材料物理性能的影响。试验结果表明:以高炉矿渣质量为基准,在碱激发剂氢氧化钠和发泡剂双氧水添加量分别为6%和2%、水固比为0.5 g/m L的情况下,添加3%的碳酸钙晶须的试件(养护时间为28 d)体积密度为0.52 g/m^3,抗压强度为1.15 MPa,导热系数为0.081 W/m·K,该材料的物理性能达到保温材料的标准。Using blast furnace slag as main raw material,Na OH as an activator,hydrogen peroxide as a pore-forming agent,and CaCO3 whisker as a modified material,a new inorganic thermal product was prepared. The influence of CaCO3 whisker dosages on physical properties of the ma-terial was discussed. The test results showed that with the quality of blasé furnace slag as a base mark,the prepared materials with thermal conductivity coefficient of 0. 081 W/m·K,compressive strength of 1. 15 MPa and bulk density at 0. 52 g/m^3 were obtained under conditions of Na OH 6%,H2O2 2%,water-solid ratio 0. 5 g/m L with the addition of CaCO3 whisker 3%( curing for 28 d).

关 键 词:高炉矿渣 碳酸钙晶须 保温材料 导热系数 体积密度 抗压强度 

分 类 号:TD926.4[矿业工程—选矿]

 

参考文献:

正在载入数据...

 

二级参考文献:

正在载入数据...

 

耦合文献:

正在载入数据...

 

引证文献:

正在载入数据...

 

二级引证文献:

正在载入数据...

 

同被引文献:

正在载入数据...

 

相关期刊文献:

正在载入数据...

相关的主题
相关的作者对象
相关的机构对象