Synthesis,Structure Characterization and Thermal Analysis of a New Cadmium Zinc Borate in the Pseudo-binary System Cd3B2O6-Zn3B2O6  

作　　者：焦志伟 段翠翠 曹雷刚 崔岩 刘峰斌 汪海军 

机构地区：[1]College of Mechanical Engineering and Materials Science,North China University of Technology [2]Gansu Research Institute of Chemical Industry

出　　处：《Chinese Journal of Structural Chemistry》2016年第11期1679-1685,共7页结构化学（英文）

基　　金：supported by the Special Foundation for Young Scientists of Beijing(No.2014000020124G009)

摘　　要：Cd-rich portion of the pseudo-binary system Cd3B2O6-Zn3B2O6 was investigated. A new cadmium zinc borate, Cd2.42Zn0.58B2O6, was synthesized successfully by a traditional solid-state reaction method. The compound crystallizes in the monoclinic space group C2/c with a = 17.3048, b = 8.4356, c = 10.2962 A^°, β = 93.157°, V = 1500.7（2） A^°3, Dc = 5.683 g/cm^3, F（000） = 2301, Z = 24, R = 0.0351 and wR = 0.0741. In its structure, BO3 triangle, CdO6 and CdO5 （or ZnO5） polyhedra are joined together by sharing bridging O atoms to form an intricate three-dimensional framework. A comparison of the structures of Cd2.42Zn0.58B2O6, α-Cd3B2O6 and β-Cd3B2O6 is presented. The IR spectrum confirms the presence of BO3 unit. The UV cut-off wavelength of Cd2.42Zn0.58B2O6 is 313 nm. The differential thermal analysis （DTA） suggests that Cd2.42Zn0.58B2O6 is an incongruent melting compound.Cd-rich portion of the pseudo-binary system Cd3B2O6-Zn3B2O6 was investigated. A new cadmium zinc borate, Cd2.42Zn0.58B2O6, was synthesized successfully by a traditional solid-state reaction method. The compound crystallizes in the monoclinic space group C2/c with a = 17.3048, b = 8.4356, c = 10.2962 A^°, β = 93.157°, V = 1500.7（2） A^°3, Dc = 5.683 g/cm^3, F（000） = 2301, Z = 24, R = 0.0351 and wR = 0.0741. In its structure, BO3 triangle, CdO6 and CdO5 （or ZnO5） polyhedra are joined together by sharing bridging O atoms to form an intricate three-dimensional framework. A comparison of the structures of Cd2.42Zn0.58B2O6, α-Cd3B2O6 and β-Cd3B2O6 is presented. The IR spectrum confirms the presence of BO3 unit. The UV cut-off wavelength of Cd2.42Zn0.58B2O6 is 313 nm. The differential thermal analysis （DTA） suggests that Cd2.42Zn0.58B2O6 is an incongruent melting compound.

关 键 词：BORATE crystal structure IR DTA 

分 类 号：O611[理学—无机化学]