玻璃粉-矿渣地聚合物基泡沫混凝土研究  

Study on geopolymer foamed concrete based on glass powder-slag

作　　者：汪海风[1] 刘杰[1] 卢建磊[1] 林州 盛建松[1] 杨辉[1,2] 

机构地区：[1]浙江大学浙江加州国际纳米技术研究院,浙江杭州310058 [2]浙江大学材料科学与工程学院,浙江杭州310027

出　　处：《新型建筑材料》2016年第12期76-79,共4页New Building Materials

基　　金：国家科技支撑计划项目(2014BAL03B01);国家863计划项目(2015AA034701)

摘　　要：以H2O2为发泡剂,以玻璃粉、矿渣、碱激发剂等为原料制备地聚合物基泡沫混凝土。考察碱激发剂模数、玻璃粉/矿渣质量比、碱激发剂用量、H2O2用量等因素对泡沫混凝土干密度、抗压强度和导热系数等性能影响。结果表明:当碱激发剂模数为1.2,玻璃粉/矿渣质量比为10%,碱激发剂用量为15%,H2O2用量为5%时,泡沫混凝土的综合性能最佳,干密度为409.3 kg/m3,抗压强度为1.64 MPa,导热系数为0.088 W/(m·K)。Using H2O2 as foam agent, geopolymer foamed concrete were prepared with glass powder, slag and alkali activator as starting materials. The experimental parameters,which affected the dry apparent density, compressive strength and thermal conductivity of foamed concrete were discussed,such as modulus of alkali activator, glass powder to slag weight ratio,alkali activator contents and H2O2 contents. The result exhibits the best properties with dry apparent density of 409.3 kg/m^3,compressive strength of 1.64 MPa and thermal conductivity of 0.088 W/（m·K） when modulus of alkali activator is 1.2,glass powder to Slag weight ratio is 10%,alkali activator content is 15%,and H2O2 content is 5%.

关 键 词：地聚合物 泡沫混凝土 玻璃粉 矿渣 

分 类 号：TU528.2[建筑科学—建筑技术科学]