Transient Liquid Phase Bonding of IN738LC/MBF-15/IN738LC:Solidification Behavior and Mechanical Properties  

作　　者：B.Binesh A.Jazayeri Gharehbagh 

机构地区：[1]Materials Research Center, Technology Development Institute,ACECR

出　　处：《Journal of Materials Science & Technology》2016年第11期1137-1151,共15页材料科学技术（英文版）

摘　　要：Transient liquid phase（TLP） bonding of IN738 LC superalloy was carried out using a rapidly solidified MBF-15 Ni-based foil. The effects of bonding temperature（1130–1170 °C） and time（5–120 min） as well as foil thickness（35–140 μm） were studied on the microstructure of joint region and its mechanical properties. The solidification sequence in the joint region was found to be（i） formation of γ solid solution in the isothermally solidified zone, followed by（ii） ternary eutectic of γ ＋ Ni3 B ＋ Cr B, and finally（iii） binary eutectic of γ ＋ Ni3 Si in the athermally solidified zone. Fine Ni3 Si particles were also formed via a solid state transformation within the γ matrix in the vicinity of eutectic products. A deviation of isothermal solidification kinetics from the standard parabolic TLP model was observed by increasing the bonding temperature to 1170 °C, which resulted in the formation of eutectic constituents at the joint centerline.The analysis of mechanical and fractographic test results revealed that the samples with complete isothermal solidification exhibit the highest shear strength, whereas the hard eutectic constituents act as preferential failure sites and lead to a significant reduction in the joint shear strength in samples with incomplete isothermal solidification.Transient liquid phase（TLP） bonding of IN738 LC superalloy was carried out using a rapidly solidified MBF-15 Ni-based foil. The effects of bonding temperature（1130–1170 °C） and time（5–120 min） as well as foil thickness（35–140 μm） were studied on the microstructure of joint region and its mechanical properties. The solidification sequence in the joint region was found to be（i） formation of γ solid solution in the isothermally solidified zone, followed by（ii） ternary eutectic of γ ＋ Ni3 B ＋ Cr B, and finally（iii） binary eutectic of γ ＋ Ni3 Si in the athermally solidified zone. Fine Ni3 Si particles were also formed via a solid state transformation within the γ matrix in the vicinity of eutectic products. A deviation of isothermal solidification kinetics from the standard parabolic TLP model was observed by increasing the bonding temperature to 1170 °C, which resulted in the formation of eutectic constituents at the joint centerline.The analysis of mechanical and fractographic test results revealed that the samples with complete isothermal solidification exhibit the highest shear strength, whereas the hard eutectic constituents act as preferential failure sites and lead to a significant reduction in the joint shear strength in samples with incomplete isothermal solidification.

关 键 词：Transient liquid phase bonding IN738LC superalloy Isothermal solidification Amorphous brazing foil Mechanical properties 

分 类 号：TG132.3[一般工业技术—材料科学与工程]