低温水热法制备竹生物炭及其对有机物的吸附性能  

Preparation of bamboo biochars by low-temperature hydrothermal method and its adsorption of organics

作　　者：李音[1,2] 单胜道 杨瑞芹[1] 盖希坤[1] 毛建卫[1] 黄宁宁 钭焱萍 Meas Arun Li Yin Shan Shengdao Yang Ruiqin Gai Xikun Mao Jianwei Huang Ningning Tou Yanping Meas Arun(Zhejiang Provincial Key Lab for Chem ＆ Bio Processing Technology of Farm Products, School of Biological and Chemical Engineering, Zhejiang University of Science and Technology, Hangzhou 310023, China Key Laboratory of Biomass Chemical Engineering of Ministry of Education, Zhejiang University, Hangzhou 310027, China)

机构地区：[1]浙江省农产品化学与生物加工技术重点实验室,浙江科技学院生物与化学工程学院,杭州310023 [2]浙江大学生物质化工教育部重点实验室,杭州310027

出　　处：《农业工程学报》2016年第24期240-247,共8页Transactions of the Chinese Society of Agricultural Engineering

基　　金：浙江省公益性技术应用研究计划项目(No.2015C33006);国家国际科技合作专项项目(No.2014DFE90040);生物质化工教育部重点实验室(浙江大学)开放基金资助项目(No.2015BCE003)

摘　　要：竹是一类常见的生物质资源,竹加工中产生的废弃物是制生物炭的理想原料。该研究采用水热炭化法,在较低的水热温度下制备竹生物炭,并通过Na OH浸泡和N2氛围下高温煅烧2种方法,对竹生物炭进行进一步改性,所得产品用于去除水溶液中2-萘酚和刚果红。结果显示:仅采用水热炭化得到的竹生物炭产品得率大于54%,表面官能团丰富,均能吸附水溶液中的2-萘酚和刚果红,其中160℃3 h下制备的样品对2-萘酚吸附效果最好,200℃7 h下制备的样品对刚果红吸附效果最好;改性处理会降低终产品得率并影响表面官能团,Na OH浸泡改性处理能增加竹生物炭对2-萘酚和刚果红的吸附容量,N2氛围下高温煅烧改性则不能提高竹生物炭对这2种物质的吸附效果。研究结果可为废弃生物质制炭及生物炭在水污染物吸附分离中的应用提供参考。Biochar is a kind of carbon-rich solid material obtained from biomass resources,which can be used as source of energy,catalyst,adsorbent and soil conditioner.Bamboo is a kind of widely used biomass resource containing high fraction of lignocellulose,and bamboo waste from industrial processing is a kind of good raw material for producing biochars.Hydrothermal carbonization approach was applied at low temperatures to produce bamboo biochars,and the selected biochar samples were further modified by being immersed in the sodium hydroxide（NaO H） solution or calcined in nitrogen atmosphere.The effects of the preparation conditions on the physico-chemical properties of the bamboo biochars were investigated,and the adsorption properties of the biochars for 2-naphthol and Congo red from their aqueous solutions were evaluated.The results showed that the yields of the bamboo biochars from hydrothermal carbonization without modification were between 54.12% and 71.53%,and the functional groups containing oxygen such as-OH（3 200-3 600 cm^-1）,C=O（1 650-1 735 cm^-1） and C-O（1 000-1 250 cm^-1） were found to be rich on the surfaces of these biochars; the oxygen content of the bamboo biochar produced at 200 ℃ and 7 h was as high as 46.33%,and the surface area of the same carbon sample was measured to be 14.10 m^2/g.The bamboo biochars modified by being immersed in the NaO H solution still showed rich oxygen-containing groups on their surfaces,high yields were also achieved with these samples,much larger surface area（33.22 m^2/g） was obtained for the biochar sample produced at 200 ℃ and 7 h and modified by soaking in NaO H solution for 1h,and the oxygen content of this carbon sample was 50.57%,which was higher than that of the sample before modification treatment.On the other hand,few functional groups were found on the surfaces of the bamboo biochars modified by calcination in nitrogen atmosphere,the yields of these biochar samples were much lower（between 12.99% and 16.21%）,even higher surface area（52.

关 键 词：生物质 吸附 炭化 竹 水热法 2-萘酚 刚果红 

分 类 号：S19[农业科学—农业基础科学]