粉青釉的研制  

Development of Blue Green Glaze

作　　者：包启富 董伟霞 周健儿 甘尊利 

机构地区：[1]景德镇陶瓷大学材料科学与工程学院,景德镇333403

出　　处：《佛山陶瓷》2017年第1期19-20,24,共3页Foshan Ceramics

基　　金：国家自然科学基金项目(51562013)

摘　　要：自制坯体,采用铁含量较高的西源土、黄坛土等为粉青釉原料在还原气氛1280~1320℃下制备了仿龙泉粉青釉。采用单因素法探讨配方组成和釉层厚度对粉青釉的影响。实验表明:当该釉配方组成为(wt%):西源22%、黄坛44%、石英16%、方解石13%、滑石5%时,釉层厚度控制在1~1.5 mm时,釉面效果与龙泉粉青釉接近。Similar imitated Longquan blue-green glaze was prepared on the home-made bodies in the reducing atmosphere of 1280-1320℃ by using XiYuan clay with high iron oxide, Huangtan clay etc. Effects of composition and glaze thickness on the blue-green glaze are studied. The results show that when the composition is Xiyuan of 22%, Huangtan of 44%, Silicon of 16%, calcite of 13% and talcum of 5 % at the thickness of 1-1.5 mm, the blue-green color of the as-prepared glaze is similar with Longquan glaze.

关 键 词：西源土 粉青釉 釉层厚度 

分 类 号：TQ174.43[化学工程—陶瓷工业]