玻璃驱水剂的研制  

Preparation on Glass Water Repellent Agent

作　　者：姜燕[1] 刘晓林[1] 许东海[1] 代伟娜[1] 李杰[1] 蔡淑红[1] 

机构地区：[1]中国船舶重工集团公司第七一八研究所,河北邯郸056027

出　　处：《舰船防化》2016年第4期45-47,共3页

摘　　要：实验以苯基硅油、异丙醇等成分为主要原料制得了一种玻璃驱水剂，并对该驱水剂的性能进行了性能测试。测试结果表明，本玻璃驱水剂液滴在玻璃片上开始下滑的平均倾斜角度为11°，在玻璃表面成膜的时间为2min，成膜后玻璃平均透光度为90％以上，经洗洁精清洗后仍有防水性，且本驱水剂样品放置3个月后无沉淀分层现象。In the experiment, a glass water repellent was prepared by using benzyl silicone oil, isopropanol and other ingredients as the main raw material. The performance had been tested. The experiments showed that the average tilt angle of the glass water repellent agent drops on the glass sheet was 1 ldegrees. The film formation time of droplet on glass surface was 2 minutes. The average transmittance of the glass after the film formation was 90% or more. After being cleaned, the glass was still waterproof. There was no sedimentation and delamination after 3 months of the water repellent agent sample.

关 键 词：玻璃 驱水剂 苯基硅油 异丙醇 

分 类 号：TQ397[化学工程]